Fabrication of cobalt-zinc bimetallic oxides@polypyrrole composites for high-performance electromagnetic wave absorption
Shixuan Feng,Hao Zhang,Haowen Wang,Rui Zhao,Xuan Ding,Huahua Su,Futian Zhai,Tingxi Li,Mingliang Ma,Yong Ma
DOI: https://doi.org/10.1016/j.jcis.2023.08.195
IF: 9.9
2023-09-04
Journal of Colloid and Interface Science
Abstract:Composite materials that combine magnetic and dielectric losses offer a potential solution to enhance impedance match and significantly improve microwave absorption. In this study, Co 3 O 4 /ZnCo 2 O 4 and ZnCo 2 O 4 /ZnO with varying metal oxide compositions are successfully synthesized, which are achieved by modifying the ratios of Co 2+ and Zn 2+ ions in the CoZn bimetallic metal–organic framework (MOF) precursor, followed by a high-temperature oxidative calcination process. Subsequently, a layer of polypyrrole (PPy) is coated onto the composite surfaces, resulting in the formation of core–shell structures known as Co 3 O 4 /ZnCo 2 O 4 @PPy (CZCP) and ZnCo 2 O 4 /ZnO@PPy (ZCZP) composites. The proposed method allows for rapid adjustments to the metal oxide composition within the inner shell, enabling the creation of composites with varying degrees of magnetic losses. The inclusion of PPy in the outer shell serves to enhance the bonding strength of the entire composite structure while contributing to conductive and dielectric losses. In specific experimental conditions, when the loading is set at 50 wt%, the CZCP composite exhibits an effective absorption bandwidth (EAB) of 5.58 GHz (12.42 GHz-18 GHz) at a thickness of 1.53 mm. Meanwhile, the ZCZP composite demonstrates an impressive minimum reflection loss (RL min ) of −71.2 dB at 13.04 GHz, with a thickness of 1.84 mm. This study offers a synthesis strategy for designing absorbent composites that possess light weight and excellent absorptive properties, thereby contributing to the advancement of electromagnetic wave absorbing materials.
chemistry, physical