Development and Performance of Urea–Formaldehyde Resin/Montmorillonite Intercalation Composite Horizontal well Plugging Agent

Nanjun Lai,Siwei Fan,Wensen Zhao,Hongwei Xu

DOI: https://doi.org/10.1007/s10553-022-01363-x

2022-03-01

Chemistry and Technology of Fuels and Oils

Abstract:Accurate identification of the water outlet point after a horizontal well has produced water is difficult, resulting in difficulty in blocking water. This article proposes improved water plugging technology for general plugging of the wellbore. In this technology, the organic polymer UF and the inorganic rigid reinforced particle MMT are combined to obtain composite at the nanometer scale for a horizontal well plugging. FIRT, XRD, TG-DSC, SEM, and other methods are used to characterize the structure of intercalated composite materials. The results show the successful MMT modification and pre-polymer synthesis reaction. The performance of the composite plugging agent is evaluated by a rotating rheometer, mechanical experiment, and plugging experiment. The initial viscosity of the plugging agent in a rheological test is 28.81 mPa·s, which shows that the plugging agent has good injectability and is not affected by shear. The solidified strength of the plugging agent material is 11.45 MPa, which meets the plugging requirements. In the core physical simulation experiment, the breakthrough pressure gradient reaches 86 MPa/m, indicating that the plugging strength of the plugging agent is high, the plugging rate is still more than 90% after 40 hours of water scouring, and the erosion resistance is strong. Compared with other plugging agents, UF-OMMT plugging agent has better thermal stability. Hence, the developed plugging agent has good application prospects.

energy & fuels,engineering, chemical, petroleum