Numerical Simulation on Refractory Wear and Inclusion Formation in Continuous Casting Tundish

Qiang Wang,Chong Tan,Ao Huang,Wen Yan,Huazhi Gu,Zhu He,Guangqiang Li

DOI: https://doi.org/10.1007/s11663-021-02097-7

2021-03-02

Metallurgical and Materials Transactions B

Abstract:<p class="a-plus-plus">The formation and removal of exogenous inclusions in a real-size two-strand tundish is simulated by the proposed unsteady 3D comprehensive numerical model of the respective fluid-structure interaction, which takes into account the impacting and washing effects on the refractory wear. A large eddy simulation is employed to describe the molten steel vortex flow. Thus, the thermal profiles of the molten steel and refractory lining are constructed. One-way coupled unsteady Euler-Lagrange approach is adopted to estimate the detachment and motion of the exogenous inclusion. The inclusion's Reynolds number is utilized for evaluating the inclusion separation at the refractory lining after formation and at the upper surface of the molten steel. At a 1.2 m/min casting speed, 49 and 38 pct of exogenous inclusions are created at the turbulent inhibitor inner bottom and long nozzle inner wall, respectively. In contrast, only 13 pct of new inclusions are produced at all other inner walls. About 80 pct of newly generated inclusions are then trapped by free surfaces, 78 pct of which are removed at the first free surface. The initial diameter of exogenous inclusions ranges from 13 to 48 <em class="a-plus-plus">μ</em>m. The removal ratio of exogenous inclusions in the tundish first grows from 61 to 80 pct, with the casting speed rising from 1.0 to 1.2 m/min and then drops to 63 pct after the further casting speed rise to 1.4 m/min.</p>