Aromatization of n-C7 ~ n-C9 Alkanes on Pt/KZSM-5(deAl) Catalyst
Qiuming Zhou,Sen Wang,Zhiwei Wu,Zhangfeng Qin,Mei Dong,Jianguo Wang,Weibin Fan
DOI: https://doi.org/10.1039/d2cy01903e
2022-12-13
Abstract:Alkane aromatization is a significant supplementary route for the preparation of value-added aromatic products. Although ZSM-5 zeolites have been widely used in alkanes aromatization, they always exhibit low catalytic stability, due to the diffusion limitation of medium-pore structure, resulting in rapid deactivation. Moreover, the excessive strong acid sites of ZSM-5 also induce serious cracking reaction. To overcome these issues, the pore structure and acidic property of ZSM-5 zeolite were controllably regulated using ammonium hexafluorosilicate (AHFS) and potassium carbonate (K2CO3) post-treatment method. After loading Pt, the Pt/KZSM-5(deAl) catalyst showed aromatic selectivity as high as 75.4%, with n-heptane conversion of 96.1%, at 550 °C and ambient pressure. More importantly, the catalytic lifetime reached 234 h. Even for the aromatization of n-octane and n-nonane with larger molecular size, the Pt/KZSM-5(deAl) still gave high aromatic selectivity of 82.7% and 83.4%, and n-octane and n-nonane conversion of 92.8% and 87.1%, along with the catalytic lifetime higher than 80 h. The results of XRD, N2 sorption, NH3-TPD, Py-IR, TEM/STEM, H2-TPR, CO-DRIFT and XPS indicated that using AHFS and K2CO3 post-treatment can not only produce more mesoporous to facilitate the diffusion of aromatic products, but also reduce the amount and strength of strong acid sites in ZSM-5 to avoid the over-cracking reaction. Moreover, the generated defect sites due to dealumination and the residual potassium ions (K+) on zeolite enhanced the interaction between Pt and ZSM-5 zeolite that effectively suppresses the aggregation and sintering of Pt particles.
chemistry, physical