Abstract:The selective catalytic reduction (SCR) technique that converts NOx from the outlet of industrial boilers at low temperature (<200 °C) requires catalysts that possess both the oxidization property of NOx and the adsorption ability to NH3. However, owing to unsuitable redox capacity, most NH3-SCR catalysts such as MnO2/TiO2 and MnO2–CeO2/TiO2 suffer from poor activity and N2 selectivity and SO2 poisoning. Benefiting from constructing mesoporous MnCeSmTiOx amorphous mixed oxides by the coprecipitation method, enhanced SO2-tolerant low-temperature NH3-SCR performance was achieved. The MnCeSmTiOx catalysts have an amorphous and mesoporous structure with a BET surface area of 214 m2·g–1. The NO conversion could reach nearly 100% at 140–320 °C and maintain >90% at 400 °C and a gas hourly space velocity of 80,000 h–1. The selectivity of N2 could be maintained at ≈100% at 100–320 °C and stay at >90% up to 400 °C. Besides, the MnCeSmTiOx catalyst preserves higher catalytic performance after introducing H2O and SO2 compared with the catalysts without adding Sm. The redox properties, acidic properties, and reaction intermediates of catalysts were analyzed by X-ray photoelectron spectroscopy, hydrogen temperature-programmed reduction, ammonia temperature-programmed desorption (NH3-TPD), O2-TPD, pyridine-IR, thermogravimetry–differential scanning calorimetry, and diffuse reflectance infrared Fourier transform. The synergistic effect of the Lewis acid sites and oxidation catalytic sites of mixed oxides serves for the conversion of NO to N2 by following the Langmuir–Hinshelwood mechanism. Doping Sm into MnCeSmTiOx can increase oxygen vacancies and transfer electrons to Mn4+ and Ce4+, which facilities the formation of active adsorbed NO2, bidentate nitrate, and bridging nitrate intermediates and suppresses SO2 poisoning by inhibiting the oxidation of SO2 by Mn4+ and Ce4+. Our work could be beneficial to modulate the redox capacity of active sites on NH3-SCR catalysts so that NOx can be eliminated in complex flue gas at low temperatures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02567?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02567</a>.Experimental details, kinetic experiments and the calculation process of the reaction rate, reaction order, and TOF; XRD patterns; TEM images; and in situ DRIFTS spectra with adsorption of NH3 NO + O2 on MnSmTiOx and CeSmTiOx catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02567/suppl_file/cs0c02567_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Effect of Tourmaline Addition on the Catalytic Performance and SO2 Resistance of NixMn3−xO4 Catalyst for NH3-SCR Reaction at Low Temperature

Effect of Tourmaline Addition on the Anti-Poisoning Performance of MnCeOx@TiO2 Catalyst for Low-Temperature Selective Catalytic Reduction of NOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

The effect of tourmaline on the denitration performance of MnOx/TiO2 catalysts and DFT calculation

Effects of Nd-modification on the Activity and SO2 Resistance of MnOx/TiO2 Catalysts for Low-Temperature NH3-SCR

Synthesis of novel Co(3-x)MnxO4@TiO2 core-shell catalyst for low-temperature NH3-SCR of NOx with enhanced SO2 tolerance

Improved Activity and SO 2 Resistance by Sm-Modulated Redox of MnCeSmTiO x Mesoporous Amorphous Oxides for Low-Temperature NH 3 -SCR of NO

The Role of the Cu Dopant on a Mn3O4 Spinel SCR Catalyst: Improvement of Low-Temperature Activity and Sulfur Resistance

Mesoporous MnOx-CeO2 composites for NH3-SCR: the effect of preparation methods and a third dopant

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Effect of Nb‐doping on the MnFeOx catalyst for NH3‐SCR reaction at low‐temperature

Promoting Effect of Ti Species in MnOx-FeOx/Silicalite-1 for the Low-Temperature NH3-SCR Reaction

Tunable Highly Dispersed Nia-xMnxAlOy Catalysts Derived from Layered Double Oxide for Low Temperature NOx Removal

Titania-Samarium-Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH3

Highly efficient NH3-SCR of NO over MnFeW/Ti catalyst at low temperature: SO2 tolerance and reaction mechanism

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Improved Activity And So2 Resistance By Sm-Modulated Redox Of Mncesmtiox Mesoporous Amorphous Oxides For Low-Temperature Nh3-Scr Of No

Low-temperature selective catalytic reduction of NO on MnOx/TiO2 prepared by different methods

Improvement of Activity and SO2 Tolerance of Sn-Modified MnOx–CeO2 Catalysts for NH3-SCR at Low Temperatures

Tuning the Property of Mn-Ce Composite Oxides by Titanate Nanotubes to Improve the Activity, Selectivity and SO2/H2O Tolerance in Middle Temperature NH3-SCR Reaction