Abstract:Polyvinylidene fluoride (PVDF) membranes are promising materials for purifying and recycling wastewater in cold regions due to their high mechanical strength and low temperature stability. However, in practical wastewater treatment services, PVDF is easily fouled by organic pollutants because of its hydrophobic charac-teristics. In addition, because of the large amount of reagent utilized in the conventional cleaning process, a new hydrophilic membrane with simple cleaning characteristics needs to be developed. In this work, a novel anti-fouling membrane (N-TiO2@PVDF) was obtained by implanting a N-TiO2 photocatalyst into a PVDF mem-brane. N-TiO2@PVDFshows a more homogeneous pore size distribution and a larger average pore diameter, which results in a higher water flux (1017.8 L/m2 & BULL;h compared to 217.4 L/m2 & BULL;h PVDF), higher model pollutant bovine serum albumin (BSA) solution flux and higher BSA rejection rate (92.3% compared to 81.4% for PVDF). Furthermore, N-TiO2@PVDF shows an outstanding hydrophilicity performance compared to the PVDF mem-brane. The water contact angle of N-TiO2@PVDF 14 decreases sharply from 93.7 (PVDF) to 53.5, and the BSA adsorption amount decreases significantly from 1.41 mg/cm2 (PVDF) to 0.05 mg/cm2. The total fouling ratio of N-TiO2@PVDF is decreased to a value of 25.5% compared to a value of 70.3% for PVDF, and the irreversible BSA fouling ratio is even decreased to 5.8% compared to 57.2% for PVDF. This result indicates that N-TiO2@PVDF shows outstanding antifouling performance. The N-TiO2@PVDF membrane also has a photocleaning function, and the BSA flux recovery ratio reaches up to 94.7% under simulated sunlight irradiation for 2 h without additional treatment. The results obtained from hydroxyl radical (& BULL;OH) detection indicate that & BULL;OH degradation of organic pollutants is the dominant mechanism for the N-TiO2@PVDF photocleaning. This anti-fouling and photocleaning N-TiO2@PVDF membrane offers a solution to wastewater treatment problems of membrane brittleness and easy fouling in cold places. It can also be a good choice for the drinking water purification process.

Tailoring the Effects of Titanium Dioxide (TiO2) and Polyvinyl Alcohol (PVA) in the Separation and Antifouling Performance of Thin-Film Composite Polyvinylidene Fluoride (PVDF) Membrane

Effect of TiO2 modified layer thickness on the properties of PVDF-TiO2 membrane

Preparation and characterization of poly (vinylidene fluoride)/TiO 2 hybrid membranes

Antifouling behaviours of PVDF/nano-TiO2 composite membranes revealed by surface energetics and quartz crystal microbalance monitoring

Preparation of Nano-TiO2-Modified PVDF Membranes with Enhanced Antifouling Behaviors via Phase Inversion: Implications of Nanoparticle Dispersion Status in Casting Solutions

Preparation of Nano-TiO 2 -Modified PVDF Membranes with Enhanced Antifouling Behaviors via Phase Inversion: Implications of Nanoparticle Dispersion Status in Casting Solutions.

Enhanced Antifouling Behaviours of Polyvinylidene Fluoride Membrane Modified Through Blending with Nano-Tio2/polyethylene Glycol Mixture

Effect of titanium dioxide nanoparticles on polyvinyl alcohol/polyvinyl pyrrolidone composite membranes

Synergistic effects of PVDF membrane surface functionalization with polydopamine and titanium dioxide for enhanced oil/water separation and photocatalytic behavior

Effects of TiO_2 Nanoparticles on the Performance of PVDF Ultrafiltration Membrane

Dye Degrading and Fouling-Resistant Membranes Formed by Deposition with Ternary Nanocomposites of N-Doped Graphene/TiO₂/Activated Carbon

Empowering TiO2–coated PVDF membranes stability with polyaniline and polydopamine for synergistic separation and photocatalytic enhancement in dye wastewater purification

Fabrication and performance evaluation of polycarbonate/polyvinyl alcohol–titanium dioxide thin‐film nanocomposite membranes for water treatment

Impact of titanium dioxide/graphene in polyvinylidene fluoride nanocomposite membrane to intensify methylene blue dye removal, antifouling performance, and reusability

Engineering a Highly Hydrophilic PVDF Membrane via Binding TiO2 Nanoparticles and a PVA Layer onto a Membrane Surface.

Fabrication of Anti-Fouling and Photocleaning PVDF Microfiltration Membranes Embedded with N-TiO2 Photocatalysts

Effect of Nano-Tio2 Particles on the Performance of Pvdf, Pvdf-G-(Maleic Anhydride), and Pvdf-G-Poly(Acryl Amide) Membranes

Preparation and Characterization of TiO2-PVDF/PMMA Blend Membranes Using an Alternative Non-Toxic Solvent for UF/MF and Photocatalytic Application

Preparation, characterization, and photocatalytic performance of polyvinylidene fluoride membrane modified with TiO2-C hybrid aerogels

Sol–gel Preparation of PAA-g-PVDF/TiO2 Nanocomposite Hollow Fiber Membranes with Extremely High Water Flux and Improved Antifouling Property

In-situ Immobilization of Titanium Dioxide on Poly (ether Ether Ketone) Hollow Fiber Membranes and the Effect of Ph Level on the Photo-Removal Process of Dyes