Hydrophilic Silver Nanoparticles for Hg(II) Detection in Water: Direct Evidence for Mercury–Silver Interaction
Irene Schiesaro,Luca Burratti,Carlo Meneghini,Ilaria Fratoddi,Paolo Prosposito,Joohyun Lim,Christina Scheu,Iole Venditti,Giovanna Iucci,Chiara Battocchio
DOI: https://doi.org/10.1021/acs.jpcc.0c06951
2020-11-15
The Journal of Physical Chemistry C
Abstract:In this work, the electronic and molecular structure, as well as the morphology, of innovative nanostructured materials whose optical properties respond to the presence of heavy metals in water samples was investigated. In particular, the here discussed silver nanoparticles (NPs) stabilized by a hydrophilic ligand (sodium 3-mercapto-1-propanesulfonate, 3MPS) are able to reveal the presence of mercury ions at ppm levels. The sensitivity of the proposed nanosensor to Hg(II) in 1–5 ppm range was ascertained by optical tests; then, the local chemistry and electronic structure of the nanostructured coordination compounds made of functionalized silver nanoparticles (NPs) and metal ions, and their correlation with the resulting nanoaggregates' shape and morphology, were investigated by state-of-the-art synchrotron radiation (SR)-induced spectroscopies and transmission electron microscopy (TEM). In particular, SR-induced X-ray photoelectron spectroscopy (XPS) and X-ray absorption spectroscopy (XAS) measurements allowed us to gather complementary information about the silver–mercury interaction, which is only partially mediated by the negatively charged 3MPS ligand, different from what was observed for analogous nanosensors applied to other bivalent heavy metal ions, for example, Co(II) and Ni(II). TEM morphological analysis sheds light on the structure of the AgNP-3MPS/Hg aggregates, revealing the formation of Ag/Hg alloy nanoparticles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.jpcc.0c06951?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.jpcc.0c06951</a>.C 1s and O 1s SR-XPS spectra of AgNP-3MPS + Hg 1 ppm and AgNP-3MPS + Hg 5 ppm (Figure S1a); C 1s, O 1s, and Hg 4f SR-XPS spectra of AgNP-3MPS + Hg 1 ppm and AgNP-3MPS + Hg 5 ppm and Ag 3d and S 2p SR-XPS spectra of AgNP-3MPS + Hg 1 ppm with the subtracted baselines reported in all spectra (Figure S1b); k<sup>2</sup>-weighted EXAFS signal measured on 1 and 5 ppm samples (Figure S2); size dispersion of AgNP-3MPS (Figure S3); size dispersion of AgNP-3MPS polluted with 1 ppm of Hg(II) (Figure S4); AgNP-3MPS with 1 ppm of Hg(II): (a) STEM image and (b) EDS map (Figure S5); EDS spectra of AgNP-3MPS with Hg(II): (a) selected areas, (b) bright field, and (c) dark field (Figure S6); and DLS data in deionized water for pristine AgNP-3MPS compared with AgNP-3MPS exposed to 5 ppm Hg(II) solution (Figure S7) (<a class="ext-link" href="/doi/suppl/10.1021/acs.jpcc.0c06951/suppl_file/jp0c06951_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical,nanoscience & nanotechnology,materials science, multidisciplinary