Stress Relaxation Behavior of Nylon 1010
LH Cai,Cheng Zhang,BH Guo,Jun Xu,ZY Huang,Li-hai Cai,Bao-hua Guo,Zhong-yao Huang
DOI: https://doi.org/10.11777/j.issn1000-3304.2016.15274
2016-01-01
Acta Polymerica Sinica
Abstract:The stress relaxation behavior of nylon 1010 samples with the initial strain of 1%, 2. 8% and 5. 1% were investigated under various temperatures for not less than 10 h. The samples were measured at 20, 40,60 and 80 degrees C separately. The stress relaxation rate, the residual stress and the activation volume under different experimental conditions were obtained. The results show that there was a certain permanent residual stress in the relaxation proCess. The reason is that the effect of the crystalline regions in the semi-crystalline nylon leads to a permanent modulus of the system. During the relaxation process, nylon samples with different initial strains showed similar trends. When the relaxation rate reached the maximum, the values of activation volume remained constant for a short period of time, which is in accordance with the principle of stress -d sigma/dt thermal activation. At this stage the activation unit of the polymer was relaxed, and the relaxation rate cicildt and the effective stress sigma* showed an exponential relation. With further relaxation, the stress decreased to a certain threshold, activation volume would gradually increase and the independent movement of activation unit was restricted. The internal stress of the polymer gradually relaxed by the cooperative movement of multiple activation units. At this final stage, the value of stress assisted work was constant. The relaxation rate -d sigma/dt and the effective stress sigma* exhibited power-law relation and the power exponent is sigma* V/(kT).