Abstract:We presented a study on the structure and magnetic properties of yttrium iron garnet (YIG), Y 3 Fe 5 O 12 , which was synthesized by means of sol–gel method and spark plasma sintering (SPS). The YIG nanoparticles were prepared by sol–gel method followed by 800 °C annealing for 3 h. SPS procedures with different temperatures (700 °C∼900 °C) and holding times (30 min ∼ 90 min) were performed to study the influence of SPS conditions on the structure and magnetic properties of YIG. The X-ray diffraction pattern and Raman spectrum confirmed the presence of YIG at all studied conditions. All samples were pure garnet phase except for the samples with too high temperatures (900 °C) and too long holding time (90 min). The impurities were inferred to be due to the hypoxic environment caused by the vacuum sintering condition of SPS. The magnetic properties of YIG samples were significantly affected by SPS conditions. The YIG sample became multi-domain at the temperature as low as 750 °C and grew to 89.1 nm at 850 °C for 30 min holding time benefiting from to the special sintering effect of SPS. Large particles with loose texture were formed by the formation of sintering neck between the adjacent particles when the SPS temperature was higher than 800 °C. It are confirmed that the sample with extended holding time at a moderate temperature (800°C/60 min) show the best soft-magnetic properties, whose M s , M r and H c are 27.5 emu/g, 2.4 emu/g and 19.2 Oe respectively. The results show that this method has good potential in preparing YIG with good magnetic properties.

Transparent magnetic fluid: preparation of YIG ultrafine particles

Synthesis and analysis of the magnetic properties of YIG by means of sol–gel and spark plasma sintering

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Influence of Surfactants on Co-Precipitation Synthesis of Bi–YIG Particles

Synthesis and Rheological Investigation of a Magnetic Fluid Using Olivary Silica-Coated Iron Particles As a Precursor

Synthesis and characterization of yttrium iron garnet (YIG) nanoparticles - Microwave material

High Saturation Magnetization, Low Coercivity and Fine YIG Nanoparticles Prepared by Modifying Co-Precipitation Method

Research on Methods of Formation of YIG Films

A New Approach of Preparing Nanocrystalline Bi-YIG Films

The Preparation and Character of Yttrium Ferrite Ferrofluid

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Study on preparation and properties of magnetic fluid

Facile Route to Γ-Fe2o3/sio2 Nanocomposite Used As a Precursor of Magnetic Fluid

Highly Lubricative, Self-Healing, Chemically Degradable, Anti-Flaming and Anti-Irradiating Magnetic Gels Simply Prepared from Binary Mixtures of Fe3O4 Nanoparticles and Water

Synthesis of Yig Nanopowders by Sol-Gel Method

Fabrication and broadband ferromagnetic resonance studies of freestanding polycrystalline yttrium iron garnet thin films

A Strategy for More Reliably Obtaining Y3Fe5O12 Thin Films with Both Low Damping and Highly Spin Transparent Surface

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

Solid Phase Synthesis and Sintering Properties of Yttrium Iron Garnet

FABRICATION OF TRANSPARENT YAG CERAMICS BY SOLID-STATE METHOD