Wear of AlCrN and CrAlSiN Coatings Applied to Nonstandard Involute Gears

Pavol Švec,Miroslav Bošanský,Ernest Gondár,František Toth,Roman Protasov

DOI: https://doi.org/10.3390/lubricants9050054

2021-05-08

Lubricants

Abstract:Wear of nonstandard involute gears with two types of coatings, AlCrN and CrAlSiN, was studied. The coatings were applied by cathodic arc deposition. The gears were tested using a Niemann tester at a graduated load up to the 12th load stage and were compared to noncoated gears. Both Biogear S150 gear oil and PP90 universal hydraulic oil were applied during these tests. The thickness of deposited coatings and wear of gear teeth were studied by SEM and their chemical compositions were determined by EDS analysis. Maximal contact pressure of 1350 MPa was calculated in the region of the tooth flank at the 12th load stage. Maximal frictional stress was also calculated on the tooth flank. The resistance against wear of gears was evaluated based on the critical weight loss and mainly based on the critical surface roughness of gears. The critical roughness was exceeded at the 10th load stage for noncoated gears. For the gears with AlCrN and CrAlSiN coatings, the critical roughness was exceeded at the 11th load stage. Wear of AlCrN and CrAlSiN coatings was nonuniform along the height of tooth. Wear on the tooth flank was characterized by fragmentation of thin coatings and subsequent detaching of fragments from the steel substrate. The steel substrate was worn by microcutting, which caused the highest roughness on the tooth surface. On the tooth pitch, surface protrusions of coatings were smoothed, and coatings cracked and locally detached subsequently. On the tooth face, surface protrusions were also smoothed but coatings remained compact without crack initiations. Both experimental oils, Biogear S150 and PP90, proved to be suitable during Niemann tests as their temperatures did not exceed the limit value of 80 °C.