Acid-Functionalized PVA Composite Membranes for Pervaporation-Assisted Esterification
Julia Agnieszka Piotrowska,Christian Jordan,Kristof Stagel,Marco Annerl,Jakob Willner,Andreas Limbeck,Michael Harasek,Katharina Bica-Schröder
DOI: https://doi.org/10.1039/d4re00388h
IF: 5.2002
2024-11-21
Reaction Chemistry & Engineering
Abstract:Composite flat sheet membranes, functionalized with imidazolium-based ionic liquids (ILs) grafted to poly(vinyl alcohol)/glutaraldehyde as catalytic layer, were developed to enhance the esterification between n-butanol and acetic acid. The functionalized membranes were produced via dip coating of commercial pervaporation membranes, and two distinct Broensted acidic ILs with imidazolium based cation and different (hydrogen sulfate [HSO 4 ] - or bromide [Br] - ) anions were compared. Compact, 12 μm thick, defect free catalytic layers were observed on top of the pervaporation membrane supports, and the determined penetration depth of ILs confirmed their presence in the upper part of coating. While both ILs could significantly promote the esterification of n-butanol and acetic acid, the [HSO 4 ] - anion catalyzed the formation of butyl acetate more effectively than [Br] - based species, resulting in yields of up to 50% over 15 hrs. Furthermore, the coated membranes exhibited enhanced water separation factors when compared to the one of unfunctionalized one, due to reduced swelling of coated membranes, accompanied by their diminished wettability.
chemistry, multidisciplinary,engineering, chemical