Abstract:A high sintering temperature is required to acquire excellent performance in the production of porcelain but results in high fuel consumption. To prepare the porcelain with outstanding performance at a lower temperature, a self-produced additive containing calcium (CaK) was added into a three-component system of kaolinite–feldspar–quartz. XRD and SEM were used to characterize the samples. The toughening mechanism and Gibbs free energy were investigated. After introducing the CaK, the bending strength of the porcelain fired at 1513 K increased from 56.32 ± 0.65 MPa to 95.31 ± 0.63 MPa, which was 21.83% higher than that of the porcelain without CaK at an optimal firing temperature of 1603 K. The main crystal phase of the sample comprised mullite and quartz in the raw materials at 1453~1603 K. The anorthite was observed at 1453 K and interlocked with needle-shaped mullite at 1513 K in the porcelain after adding CaK, which resulted in the higher bending strength. Quantitative analysis indicated that the amount of anorthite decreased at 1513 K and disappeared at 1543 K; the amount of mullite increased with temperature. The Gibbs free energy of the reaction (CaO•Al2O3•2SiO2 + 2(Al2O3•2SiO2) → 3Al2O3•2SiO2 + CaO + 4SiO2) at high temperature was negative, which suggested that the formation of mullite (3Al2O3•2SiO2) from anorthite (CaO•Al2O3•2SiO2) was possible. These findings implied that the addition of CaK contributed to the appropriate phase composition and microstructure, and the excellent performance of the porcelain at a lower temperature. In addition, the transformation between anorthite and mullite was possible in the special raw material system. The results are of interest in producing anorthite/mullite ceramics at reduced sintering temperatures and the conversion between anorthite and mullite.

Effects of Temperature and Duration of Anorthite Synthesis from Mixtures of Kaolin and Calcite

Impact of the Mineral Composition and Sintering Temperature on the Synthesis of Anorthite Ceramics

The influence of different CaO source in the production of anorthite ceramics

Influence of Annealing Temperature on Microstructure and Phase Transformations of Oxide System Bi2O3/TiO2 Formed in Aqueous Solutions

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

The Effect of Calcination Temperature on the Structure and Performance of Nanocrystalline Mayenite Powders

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

High-temperature Phase Transition and Local Structure of a Hydrous Anorthoclase

Gehlenite and anorthite crystallisation from kaolinite and calcite mix

Synthesis And Growth Of Anorthite Crystal During In Situ Preparation Of Porous Anorthite Ceramics By Foam-Gelcasting

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Effect of temperature and magnesia on phase transformation kinetics in stoichiometric and non-stoichiometric cordierite ceramics prepared from kaolinite precursors

Influence of calcination temperature on the physical and chemical characteristics of kaolinitic clays for use as supplementary cementitious materials

Effect of Calcination Temperature on the Phase Composition, Morphology, and Thermal Properties of ZrO2 and Al2O3 Modified with APTES (3-aminopropyltriethoxysilane)

Preparation of Anorthite/Mullite In Situ and Phase Transformation in Porcelain

Effects of hydrothermal temperature on formation and decoloration characteristics of anatase TiO 2 nanoparticles

Investigating the effects of calcination temperature on porous clay heterostructure characteristics

Synthesis of Precipitate Calcium Carbonate with Variation Morphology from Limestone by Using Solution Mixing Method

Effect of Reaction Condition on Crystallization Behavior of NaX Sieve

Anorthite ceramics: grog and clay selection for lowering the sintering temperature