Characterization and Tribological Properties of W-Ti-N/Al-Si Multilayer Surface Coating for Iron Alloy Pistons

Khaled Chemaa,Salim Hassani,Mohamed Gaceb

DOI: https://doi.org/10.1007/s11665-021-05996-7

IF: 2.3

2021-06-28

Journal of Materials Engineering and Performance

Abstract:Piston skirts undergo important wear and abrasion due to poor tribological properties. A surface coating system with appropriate friction and hardness properties is proposed in this work to enhance the base material durability of iron alloy pistons. Aluminum-Silicon (Al-Si) thin film was deposited using vacuum evaporation process from 85 at.% Al and 15 at.% Si powders. The W-Ti-N thin film was deposited on the top of the Al-Si thin film using a PVD sputtering process from a W-Ti (70 at.% W and 30 at.% Ti) target onto a stainless steel substrate. The microstructural, mechanical and tribological properties of the multilayer were studied for potential applications on piston skirts manufactured from iron alloys. W-Ti-N/Al-Si multilayer shows a dense microstructure morphology with W2N (200) is the main phase present. Hardness measurements indicate that Al-Si thin film reached a value of 8.8 ± 0.37 GPa, while that of W-Ti-N/Al-Si multilayer reaches values as high as 17.2 ± 0.25 GPa. Tribological tests conducted on the multilayer system revealed interesting results, namely the very low values of the friction coefficient reaching μ ≈ 0.084±0.018 and that of the wear rate showing a value of k <8.7 ± 0.1·10-13 m3/N·m. Results from the present study are promising and provide an good alternative approach toward the reduction of important energy losses related to friction of the iron alloys piston skirts.

materials science, multidisciplinary