Comparative study of structural and superconducting properties of (Cu0.5Tl0.5)Ba2Ca2Cu3O10-δ phase substituted by copper fluoride and thallium fluoride

A. Kamar,A. Srour,M. Roumié,W. Malaeb,R. Awad,A. Khalaf

DOI: https://doi.org/10.1007/s00339-021-04707-2

2021-07-05

Applied Physics A

Abstract:<p class="a-plus-plus">A series of (Cu<sub class="a-plus-plus">0.5−<em class="a-plus-plus">x</em></sub>Tl<sub class="a-plus-plus">0.5−<em class="a-plus-plus">y</em></sub>)-1223 superconductor samples, doped with varying amounts of (CuF)<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub> and (TlF)<sub class="a-plus-plus"><em class="a-plus-plus">y</em></sub> compounds with <em class="a-plus-plus">x</em> = <em class="a-plus-plus">y</em> = 0.0, 0.1, 0.2, 0.3 and 0.4, were synthesized via a single-step solid-state reaction. X-ray diffraction (XRD) revealed that all the samples have a tetragonal symmetry of (Cu<sub class="a-plus-plus">0.5</sub>Tl<sub class="a-plus-plus">0.5</sub>)-1223 phase. Additionally, with increasing fluorine content up to <em class="a-plus-plus">x</em> = 0.2 CuF and <em class="a-plus-plus">y</em> = 0.1 TlF, the phase fraction and the superconducting transition <em class="a-plus-plus">T</em><sub class="a-plus-plus"><em class="a-plus-plus">c</em></sub> were enhanced. The scanning electron microscopy (SEM) images exhibited mainly plate-like rectangular shape grains confirming the formation of (Cu<sub class="a-plus-plus">0.5</sub>Tl<sub class="a-plus-plus">0.5</sub>)-1223 phase. The Fourier transform infrared (FTIR) spectra of CuF- and TlF-substituted (Cu<sub class="a-plus-plus">0.5−<em class="a-plus-plus">x</em></sub>Tl<sub class="a-plus-plus">0.5−<em class="a-plus-plus">y</em></sub>)-1223 show a slight softening and hardening in few peaks related to the apical oxygen atoms and CuO<sub class="a-plus-plus">2</sub> planar modes. The stoichiometry of elemental composition for all prepared samples has been confirmed using ion beam analysis (IBA) methods. The excess conductivity Δ<em class="a-plus-plus">σ</em> above <em class="a-plus-plus">T</em><sub class="a-plus-plus"><em class="a-plus-plus">c</em></sub> was analyzed through the Aslamasov–Larkin (AL) approach. Using the Ginzburg–Landau (GL) number (N<sub class="a-plus-plus">G</sub>) and equations, the coherence length, the effective layer thickness, the lower critical field B<sub class="a-plus-plus">c1</sub>(0), the upper critical field B<sub class="a-plus-plus">c2</sub>(0) and the critical current density J<sub class="a-plus-plus">c</sub>(0) were estimated. It was found that the addition of an optimum concentration of CuF and TlF, controlled the microstructure, the grains coupling and hence enhanced the physical properties of (Cu<sub class="a-plus-plus">0.5</sub>Tl<sub class="a-plus-plus">0.5</sub>)-1223 phase.</p>