Phase formation and superconducting properties of (Tl,M)(Sr, Ba)Ca3Cu4Oz compounds with M = Ca, Mg, and Cu
Ho Keun Lee,Sangmin Park,Ji Won Seo,Roslan Abd-Shukor
DOI: https://doi.org/10.1007/s10854-024-12390-1
2024-03-21
Journal of Materials Science Materials in Electronics
Abstract:Polycrystalline samples of (Tl 1− x M x )SrBaCa 3 Cu 4 O z ((Tl, M)-1234), where M = Ca, Mg and Cu, were prepared by using a solid state reaction method to find the environmentally friendly element that promotes the formation of the 1234 phase. X-ray diffraction data showed that Ca substitution was very effective in forming the 1234 phase at normal pressure, compared to either Mg or Cu substitution. Nearly single-phase samples were obtained for the nominal compositions of (Tl 1− x Ca x )SrBaCa 3 Cu 4 O z (0.3 ≤ x ≤ 0.5) and (Tl 0.7 Ca 0.3 )(Sr 2− y Ba y )Ca 3 Cu 4 O z (1.0 ≤ y ≤ 1.25). The (Tl 0.7 Ca 0.3 )(Sr 2− y Ba y )Ca 3 Cu 4 O z (1.0 ≤ y ≤ 1.25) samples were found to have a relatively homogeneous microstructure by scanning electron micrography. Bulk superconductivity with T c of 102 K was observed in the (Tl 0.7 Ca 0.3 )SrBaCa 3 Cu 4 O z sample. The experimental results suggest that Ca can be a very useful element in the charge reservoir layer to form a single-phase Tl-1234-type compound with appropriate substitution of Ba into the Sr sites in the bridging layer.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied