Fast and highly reversible Na+ intercalation/extraction in Zn/Mg dual-doped P2-Na0.67MnO2 cathode material for high-performance Na-ion batteries

Xiaoqin Huang,Deli Li,Haijian Huang,Xiao Jiang,Zeheng Yang,Weixin Zhang

DOI: https://doi.org/10.1007/s12274-021-3715-2

IF: 9.9

2021-07-08

Nano Research

Abstract:<p class="a-plus-plus">P2-type layered Na<sub class="a-plus-plus">0.67</sub>MnO<sub class="a-plus-plus">2</sub> has been considered to be a promising candidate cathode material for sodium ion batteries. Nevertheless, the undesired phase transitions during operation and the large Na<sup class="a-plus-plus">+</sup> radius induced sluggish ion diffusion remain the stumbling blocks to realize its high performance. Herein, we propose a Zn/Mg co-doping strategy, which is proved to have bifunctional effects. First, relative to the pristine P2-Na<sub class="a-plus-plus">0.67</sub>MnO<sub class="a-plus-plus">2</sub> and the single-ion (Zn/Mg) doped samples, the Zn/Mg dual-doped P2-Na<sub class="a-plus-plus">0.67</sub>MnO<sub class="a-plus-plus">2</sub> demonstrates a lower Mn<sup class="a-plus-plus">3+</sup>/Mn<sup class="a-plus-plus">4+</sup> ratio and a higher lattice O content, which facilitate the structural stability of the cathode material. More intriguingly, the Zn/Mg co-doping gives rise to enlarged interplanar spacing, which provides spacious ion diffusion channels for fast Na<sup class="a-plus-plus">+</sup> intercalation/extraction. As a result, the Zn/Mg dual-doped sample exhibits a high Na<sup class="a-plus-plus">+</sup> diffusion coefficient and a solid-solution reaction during charge/discharge, with a cell volume change determined to be only 0.55%. Taking advantages of the above favorable features, the Zn/Mg dual-doped P2-Na<sub class="a-plus-plus">0.67</sub>MnO<sub class="a-plus-plus">2</sub> demonstrates a high rate performance with 67.2 mAh·g<sup class="a-plus-plus">−1</sup> delivered at 10 C and a decent cycling stability with a capacity retention of 93.8% achieved at 1 C after 100 cycles. This work introduces the Zn/Mg co-doping strategy to simultaneously improve the cycling stability and rate capability of P2-Na<sub class="a-plus-plus">0.67</sub>MnO<sub class="a-plus-plus">2</sub>, which may offer a promising avenue for further performance enhancement of the layered Na-ion batteries cathode materials. </p>

materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology