Microstructure evolution and nano-phases strengthening of Al-5%Cu alloy by adding trace AlSiTiCrNiCu high entropy alloy
Qinglin Li,Yushi Zhang,Xiaoyu Zhang,Shang Zhao,Yefeng Lan,Tiandong Xia,Xiaowu Hu
DOI: https://doi.org/10.1016/j.matchar.2021.111100
IF: 4.537
2021-05-01
Materials Characterization
Abstract:<p>In the present work, AlSiTiCrNiCu high entropy alloy (HEA) has been used in as-cast Al-5wt%Cu alloy to investigate the effect of HEA addition level (0.3 wt% and 0.6 wt%) on the microstructure and mechanical performance. The results revealed that the addition of HEA has a distinct influence on the size and morphology of primary α-Al and second phases in the cast Al-5wt%Cu alloy. When 0.3 wt% and 0.6 wt% HEA was added to Al-5wt.%Cu alloy, the primary α-Al dendrites was obviously refined and the mean size of α-Al grains was significantly reduced from 372.5 μm to 183.4 μm and 156.3 μm, respectively. Meanwhile, the size and morphology of θ-Al<sub>2</sub>Cu phases distributed inter-dendritic zone occurred to obvious change with increase of HEA addition concentration. In addition, the θ-Al<sub>2</sub>Cu phases disappeared and eutectic Al<sub>3</sub>CuNi phases precipitated after adding the HEA in Al-5wt.%Cu alloy. Compared with θ-Al<sub>2</sub>Cu phases, the width was decreased and the continuity of Al<sub>3</sub>CuNi was improved when HEA was added to Al-5wt.%Cu alloy. Moreover, it was found by TEM that some novel nano-particles precipitated from Al-5wt%Cu alloy with the addition of HEA in solidification, which uniformly distributed in the α-Al matrix. The yield strength, ultimate tensile strength and elongation of Al-5wt%Cu alloy with 0.6 wt.% HEA addition were significantly increased by 19.7%, 20.1% and 92.3%, respectively. The improvement of mechanical properties was attributed to change of morphology and decreasing size of α-Al and Al<sub>3</sub>CuNi phases. In addition, a new plate-like structure precipitated which morphology is similar to θ' phase and multi-elements nano-particles formed, which strengthened the Al-5wt.%Cu alloy.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing