Luminescence properties of blue-emitting Ce3+-doped series of Ca2Al2SiO7 and Sr2Al2SiO7 phosphors

Tripti Richhariya,Nameeta Brahme,D. P. Bisen,Yugbodh Patle,Ekta Chandrawanshi,Nikeeta Shah

DOI: https://doi.org/10.1007/s10854-021-06593-z

2021-07-19

Abstract:<p class="a-plus-plus">Ce<sup class="a-plus-plus">3+</sup>-doped series of Ca<sub class="a-plus-plus">2</sub>Al<sub class="a-plus-plus">2</sub>SiO<sub class="a-plus-plus">7</sub> and Sr<sub class="a-plus-plus">2</sub>Al<sub class="a-plus-plus">2</sub>SiO<sub class="a-plus-plus">7</sub> are prepared via conventional high-temperature solid-state reaction method and impact of Ce<sup class="a-plus-plus">3+</sup> doping on Fracto-mechanoluminescence (ML) and Photoluminescence (PL) properties of Ca<sub class="a-plus-plus">2</sub>Al<sub class="a-plus-plus">2</sub>SiO<sub class="a-plus-plus">7</sub> and Sr<sub class="a-plus-plus">2</sub>Al<sub class="a-plus-plus">2</sub>SiO<sub class="a-plus-plus">7</sub> was analyzed. Identification of phase formation was done by XRD. Analysis of PL studies reveals that both phosphors emit broadband in the intense blue region, when excited by near-UV light (356 nm), and for further analysis, the emission band was resolved into two peaks, which was attributed to <sup class="a-plus-plus">2</sup>D<sub class="a-plus-plus">3/2</sub> → <sup class="a-plus-plus">2</sup>F<sub class="a-plus-plus">5/2</sub> and <sup class="a-plus-plus">2</sup>D<sub class="a-plus-plus">3/2</sub> → <sup class="a-plus-plus">2</sup>F<sub class="a-plus-plus">7/2</sub> transitions of Ce<sup class="a-plus-plus">3+</sup> ion. The calculated energy difference between these two peaks was found to be 1979 cm<sup class="a-plus-plus">−1</sup> and 2037 cm<sup class="a-plus-plus">−1</sup>, which were in good agreement with the theoretical energy difference (~ 2000 cm<sup class="a-plus-plus">−1</sup>). The color purity of prepared phosphors was much better than commercial BAM (BaMgAl<sub class="a-plus-plus">10</sub>O<sub class="a-plus-plus">17</sub>: Eu<sup class="a-plus-plus">2+</sup>) phosphor. ML studies were also performed and effect of radiation dose on ML sensitivity has been studied. Results suggest that synthesized phosphors were applied to damage sensors and display devices.</p>