Single-sided ultrasonic welding of carbon fiber/Nylon 66 composite

Qian Zhi,Jin-Ming Ma,Xin-Rong Tan,Zhong-Xia Liu,Zeng-Guo Tian,Pei-Chung Wang

DOI: https://doi.org/10.1007/s40194-021-01161-9

IF: 2.1

2021-07-17

Welding in the World

Abstract:In this study, the weldability of single-sided ultrasonic welding of 4-mm-thick carbon fiber/Nylon 66 composite was studied. Extensive welding was performed, and the weld microstructures, fractographies, and appearances of welded joints were examined and analyzed. It was found that the strengths of single-sided ultrasonic welded (SSUWed) joints made with proper welding variables are comparable to that of the ultrasonic welded joints. The solid SSUWed joints with introducing a gap of 1.0 mm can be produced with the use of double-pulse ultrasonic vibration schedule. The robust welding variables include a weld pressure of 0.17 MPa and a weld time of 1.3 s for the first vibration pulse, 5-s cooling, and a weld time of 1.3 s for the second vibration pulse. Microstructure analyses and mechanical testing of the welds revealed that the application of second ultrasonic pulse caused the melting of the materials at periphery of the existing weld, and consequently resulted in an increase in weld area. The use of the second vibration pulse not only improved the strength but also decreased the scatter in strength of the ultrasonic welded 4-mm-thick carbon fiber/Nylon 66 composite. The double-pulse vibration schedule improves the robustness of the SSUW and increases the flexibility of product designs that rely on the ultrasonic welding for assembly.

metallurgy & metallurgical engineering