Friction stir spot welding of 5052 aluminum alloy to carbon fiber reinforced polyether ether ketone composites

Honggang Dong,Zuyang Tang,Peng Li,Baosheng Wu,Xiaohu Hao,Chaoqun Ma

DOI: https://doi.org/10.1016/j.matdes.2021.109495

2021-03-01

Abstract:<p>The hybrid structure composed of aluminum alloy and carbon fiber reinforced plastics could combine their advantages. In order to investigate the weldability of these two lightweight materials, the hybrid joints of 5052 aluminum alloy (AA5052) and carbon fiber reinforced polyether ether ketone composites (CF-PEEK) were fabricated by friction stir spot welding. The variance analysis revealed that the dwell time and plunge speed were the most significant factors. By optimizing the welding parameters, the ultimate tensile shear load reached 2690±64 N (the dwell time: 8 s, the plunge speed: 10 mm/min). The interface could be divided into pin-affected zone, shoulder-affected zone, resin adhesive zone and resin concentrated zone. Since resin concentrated zone could not provide interfacial bonding due to delamination, the shoulder-affected zone and pin-affected zone were decisive regions for mechanical properties. The bonding mechanism included three parts: adhesive bonding provided by re-solidified resin, macro-mechanical interlocking of aluminum alloy that entered CF-PEEK, and micro-mechanical interlocking of resin that was tightly trapped at surface slits as well as the carbon fibers beset into AA5052. This work clarifies the interfacial characteristics of AA5052/CF-PEEK hybrid joints and provides an approach to improve the mechanical properties.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The problem this paper attempts to address is: how to effectively join 5052 aluminum alloy with carbon fiber reinforced polyether ether ketone composite (CF-PEEK) using friction stir spot welding (FSSW) technology, and optimize welding parameters to improve the mechanical properties of the joint.

Specifically, the paper focuses on the following aspects:
1. **Welding Process Optimization**: Investigate the effects of welding parameters such as rotational speed, dwell time, and plunge speed on the mechanical properties of AA5052/CF-PEEK hybrid joints through full factorial experimental design and analysis of variance.
2. **Interface Characteristics Analysis**: Explore the interface characteristics and bonding mechanisms of AA5052/CF-PEEK hybrid joints using thermogravimetric analysis, optical microscopy, and scanning electron microscopy.
3. **Mechanical Properties Evaluation**: Evaluate the mechanical properties of the joints under different welding parameters through tensile shear tests, and analyze the relationship between effective bonding area and tensile shear load.

The main objective of the paper is to improve the mechanical properties of AA5052/CF-PEEK hybrid joints by optimizing welding parameters and understanding interface characteristics, thereby providing technical support for the application of lightweight materials in the automotive industry.