Abstract:The mass loss kinetics of thermally modified wood species was analyzed as a time–temperature function. European beech (Fagus sylvatica L.), English oak (Quercus robur L.), Norwegian spruce (Picea abies L. Karst.) and Scots pine (Pinus sylvestris L.) wood specimens of dimensions 20 × 20 × 10 mm3 were thermally modified at 140 °C, 160 °C, 180 °C, 200 °C and 220 °C for 1–6 h using atmospheric pressure and superheated steam environment. The process intensity was determined by mass loss (ML), based on oven-dry mass before and after the thermal modification. Furthermore, the equilibrium moisture content (EMC) was determined before and after thermal modification to analyze the effect of mass loss on the sorption properties. Measured mass loss data were compared with the three-dimensional analytical function and its applicability to mass loss prediction was verified. For the studied wood species, the ML was found to be less than 1–1.5% when temperature of 140 °C and 160 °C was applied. Differences between studied species were more significant at temperatures higher than 160 °C. With the highest tested temperature (220 °C), mass loss reached 13.5% (beech), 18.8% (oak), 6.7% (spruce) and 13.5% (pine). According to the results, hardwoods have been shown to be more sensitive to the thermal degradation than softwoods as demonstrated by the higher mass loss recorded for the same modification time and temperature. The three-dimensional analytical function was confirmed as valid for all the species studied (R2 = 0.89–0.99) and relevant for the mass loss prediction using fitted parameters. The EMC was reduced after thermal modification within the range of 4–48%, 0.4–47%, 1–32% and 0.7–40% for beech, oak, spruce and pine, respectively. Further, the EMC correlates exponentially (R2 = 0.91–0.95) with the decrease in the specimens' mass depending on the wood species used and modification temperature applied. However, the EMC seems to be almost stabilized beyond a limit value of approximately 10–12% of mass loss. The results provide a better insight into the mass loss and EMC kinetics of thermally modified wood species and can be used as a tool for prediction of mass loss values and required material properties (EMC) for designed wooden products.

Electrical resistance characteristics of thermally modified wood

Theoretical and Experimental Study on Transient Measurement of Wood Thermal Properties

The prediction of effective thermal conductivities perpendicular to the fibres of wood using a fractal model and an improved transient measurement technique

Effect of natural weathering on water absorption and pore size distribution in thermally modified wood determined by nuclear magnetic resonance

Small resistive wood moisture sensors: a method for moisture content determination in wood structures

Establishment of moisture diffusion regularities through the polymer shell of thermally modified wood

Mass loss kinetics of thermally modified wood species as a time–temperature function

Rapid assessment of physical properties and chemical composition of thermally modified wood by mid-infrared spectroscopy

Swelling kinetics of thermally modified wood

Thermal properties of wood: measurements by transient plane source method in dry and wet conditions

Performance of Thermally Modified Spruce Timber in Outdoor Above-Ground Conditions: Checking, Dynamic Stiffness and Static Bending Properties

Correlation analysis between mass loss of wood due to thermal modification and equilibrium moisture content of thermally modified wood

Color as an Indicator of Properties in Thermally Modified Scots Pine Sapwood

Changes in sorption and electrical properties of wood caused by fungal decay

Thermal Modification of Spruce and Maple Wood for Special Wood Products

The effect of temperature and moisture content on drilling resistance measurements in wood (Pinus sylvestris L.)

The behavior of thermally modified wood after exposure in maritime/industrial and urban environments

THE EFFECT OF MOISTURE CONTENT ON ELECTRICAL PROPERTIES OF SELECTED SOFTWOODS; CEDAR, JUNIPER, AND PINE

Experimental Measurements of Thermal Conductivity of Wood Species in China: Effects of Density, Temperature, and Moisture Content

Experimental Study of the Anisotropic Thermal Conductivity of Spruce Wood

Dimensional stability and equilibrium moisture content of thermally modified hardwoods