Use of Mixture Design Approach for the Optimization and Performance of Cost-Effective Cementitious Quaternary System: Portland Cement–Fly Ash–Silica Fume–Phosphogypsum

Khaoula Mkadmini Hammi,Halim Hammi,Ahmed Hichem Hamzaoui

DOI: https://doi.org/10.1007/s42250-021-00262-8

2021-07-30

Chemistry Africa

Abstract:The present study investigated the effect of partial Portland cement replacement by mineral admixtures including silica fume, fly ash and purified phosphogypsum at different proportions on the mechanical properties of mortar such as compressive strength and flexural strength, and on the initial setting time using the mixture design approach. This research aims to save environment from pollution with recycling solids wastes materials especially fly ash and phosphogypsum in cement building as well as to improve more the mechanical strength of ordinary Portland cement and to accelerate the initial setting time for specific applications. Based on response surface methodology, a compromise between setting time, compressive strength and flexural strength was successfully found and the optimum proportions of different constituents are as follows: 85.3% of cement, 3% of purified phosphogypsum, 6.7% of silica fume and 5% of fly ash. These conditions allow the development of cement with initial setting time of 111.2 min, compressive strength of 49.54 MPa and flexural strength of 18.85 MPa which are more important than that of the ordinary Portland cement. Interestingly, the development of compressive strength at curing ages with incorporation of pozzolans indicated that inclusion of combined pozzolans increases the 28 days strength significantly compared to cement reference. This behavior was observed through the scanning electron microscopy.

English Else