Formation mechanism of defect metal hydrides containing superabundant vacancies

Yuh Fukai,Hidehiko Sugimoto
DOI: https://doi.org/10.1088/0953-8984/19/43/436201
2007-09-26
Abstract:The formation of defect hydrides containing a large number of M-atom vacancies (superabundant vacancies; SAVs) was studied in bcc NbHx and in the fcc phase of FeHx, CoHx, NiHx and PdHx, by resistivity and XRD measurements under different conditions of hydrogen pressure and temperature, with/without allowing for exchange of hydrogen with environment (open-/closed-system methods). Two distinctly different behaviors were observed: in metals with small formation energy of Vac–H clusters, both H and vacancies enter abundantly into the M-lattice to form the ultimate defect-ordered structure, whereas in metals with relatively large formation energies, vacancy concentrations remain relatively small. This general trend was examined by Monte Carlo simulations based on a lattice–gas model. The result showed the occurrence of two distinct phases in the vacancy distribution caused by the combined action of the long-range elastic interaction and local Vac–H interactions, in accordance with the observation. Conditions for the occurrence of these 'vacancy-rich' and 'vacancy-poor' states are examined.
What problem does this paper attempt to address?