Abstract:The segregation of hydrogen and vacancies at the Σ5(210)[001] symmetric tilt grain boundary (GB) was studied by atomic scale simulations in Ni. First, the hydrogen segregation energies and hydrogen–hydrogen pair interaction energies were calculated on every interstitial site of the GB. The vacancy–hydrogen clusters' formation energies were also determined on the most favorable site. All these calculations were done using the density functional theory. Second, based on these elementary energies, a free energy functional was built to determine the concentration of segregated hydrogen and of vacancy-hydrogen clusters, as a function of the bulk hydrogen concentration and the temperature. It was found that two configurations exits in typical conditions where embrittlement is observed experimentally: H segregation only, with up to 3 hydrogen atom per structural unit or 50% occupancy by VH 5 clusters (1 cluster every two structural unit). The cohesive stress and ideal work of fracture were evaluated by fracturing the GB with different degrees of hydrogen and vacancy segregation. H segregation alone (no vacancy) decreased the work of fracture by 25%. A significantly larger decrease of cohesion was obtained when considering vacancy-hydrogen clusters. A maximum drop of the cohesive stress, of a magnitude of 40%, was obtained when every structural unit was hosting a VH 4 cluster. Finally, these data were transformed into cohesive stress models. They were used to evaluate the degree of localization of the shear displacement at the crack tip. The conclusion is that, even if cohesion is very significantly decreased, shear localization is still effective, meaning that dislocation emission should occur at the expense of crack propagation. The comparison with other grain boundaries in the literature shows that the GB studied is almost an ideal sink and therefore is very favorable for the formation of equilibrium VH n . It represents more an upper bound of the effect. Therefore, extra ingredients should be considered to explain the embrittlement observed experimentally.

Hydrogen-enhanced grain boundary vacancy stockpiling causes transgranular to intergranular fracture transition

Hydrogen-induced transgranular to intergranular fracture transition in bi-crystalline nickel

Molecular Dynamics Studies of Hydrogen Effect on Intergranular Fracture in Α-Iron

Special Fracture Behavior of Nanocrystalline Metals Driven by Hydrogen

Study on the Effects of H on the Plastic Deformation Behavior of Grain Boundaries in Nickle by MD Simulation

A Coupled Diffusional-Mechanical Model Accounting for Hydrogen Enhancements of Strain-Induced Dislocations and Vacancies

Hydrogen-Induced Dislocation Nucleation and Plastic Deformation of ⟨001⟩ and ⟨11¯0⟩ Grain Boundaries in Nickel

The effects of hydrogen and vacancy on the tensile deformation behavior of Σ3 symmetric tilt grain boundaries in pure fe

Special Fatigue Fracture Behavior of Nanocrystalline Metals under Hydrogen Conditions

Hydrogen Embrittlement Prompt Fracture in Ni-based Single Crystal Superalloy

Atomistic investigation of hydrogen induced decohesion of Ni grain boundaries

Effect of Multiple Hydrogen Embrittlement Mechanisms on Crack Propagation Behavior of FCC Metals: Competition Vs. Synergy

Hydrogen-Induced Dislocation Nucleation and Plastic Deformation of < 001 > and < 1(1)over-bar0 > Grain Boundaries in Nickel

Segregation of hydrogen and vacancies at the Σ5(210)[001] symmetric tilt grain boundary in Ni and influence on cohesion

Hydrogen-enhanced interfacial damage in Ni-based single crystal superalloy

Hydrogen-Enhanced Dislocation Activity And Vacancy Formation During Nanoindentation Of Nickel

The in-situ TEM observation of microcrack nucleation in titanium aluminide

Studying Crack Propagation along Symmetric Tilt Grain Boundary with H Segregation in Ni by MD Simulation

Hydrogen diffusion behavior within microstructures near crack tip: A crystal plasticity study

Hydrogen Effect on the Intergranular Failure in Polycrystal Ɑ-Iron with Different Crystal Sizes

Key role of interaction between dislocations and hydrogen-vacancy complexes in hydrogen embrittlement of aluminum: discrete dislocation plasticity analysis