Correlation Between the Pseudo-Capacitance Behavior and the Second-Order Phase Transition in the Li+Insertion/Desertion in Cu3Si
Aodi Shi,Si Chen,Songsheng Zheng,Zhaolin Wang
DOI: https://doi.org/10.6023/a21080363
2021-01-01
Abstract:Lithium-ion batteries with high energy density have urgent demand, especially in the fields of pure electric vehicles, smart phones, laptops, wind power generation and energy storage. Therefore, more and more attention has been paid on materials with high energy density, rapid charge/discharge capability and long cycle life. In this paper, pure Cu3Si phase was prepared by metallurgical process, and the electrochemical characteristics of the as prepared Cu3Si samples were studied by using CR2025 button half-cell structure with metal lithium sheet as reference electrode and Celgard 2500 as diaphragm. The results showed that, at a current density of 0.1C (420 mA.g(-1)), it possessed a first-cycle discharge specific capacity of 759 mAh.g(-1) with a coulomb efficiency of 96.56%. It remained 822 mAh.g(-1) after 200 cycles with a capacity retention rate of 98%. It retained 776, 700, 580, 500, 440 and 405 mAh.g(-1) at a testing rate of 0.1C, 0.2C, 0.4C, 0.6C, 0.8C and 1C, respectively. The specific capacity was stabilized at around 790 mAh.g(-1) when the current density was restored to 0.1C, which did not decrease significantly compared with the initial value. Moreover, the impedance was about 60 Omega, lower than that of the reported Si@C anode. Thus, it suggested that introducing Cu would greatly reduce the charge transfer resistance. It was worth noting that the charge/discharge curve was slope like and had pseudo capacitance characteristics. Furthermore, the cyclic voltammetry (CV) measurement was carried out at scanning rates of 0.1, 0.2, 0.4, 0.6, 0.8 and 1.0 mV/s, respectively. The results discovered for the first time that the as-prepared Cu3Si possessed the characteristic of both battery and capacitance. They together stored the charges, and the capacitance dominated the contribution. Moreover, an clear step could be observed at 550-600. in the differential scanning calorimetry (DSC) curve of the as-prepared Cu3Si sample after discharged, relating to a change in the specific heat capacity. Moreover, the sample phase did not change before and after the charge/discharge process. Therefore, it was determined that the Li+ insertion/desertion process of Cu3Si was not a first-order phase transition but a second-order phase transition process. To be concluded, for Cu3Si anode materials, the redox process was a second-order phase transition, which exhibited a pseudo capacitive behavior in its electrochemical properties.