Formulation of captopril-loaded hydrogel by microwave-assisted free radical polymerization and its evaluation

Furqan Muhammad Iqbal,Sarah Iqbal,Bushra Nasir,Waseem Hassan,Hammad Ahmed,Syed Yasir Iftikhar

DOI: https://doi.org/10.1007/s00289-021-03867-8

IF: 2.843

2021-08-31

Polymer Bulletin

Abstract:Copolymeric hydrogel was prepared by crosslinking polyvinyl alcohol (PVA) with 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS). The crosslinking of polymers was assisted by microwave radiation using N,N′-methylenebisacrylamide (MBA) as crosslinker and very low quantities of potassium persulfate (KPS) as initiator. The prepared hydrogels were loaded with captopril and subjected to in vitro and in vivo evaluation. The swelling studies were performed at pH 2 and pH 7.4 to determine water absorption at lower and higher pH. The hydrogel formulations with higher proportions of AMPS and appropriate dose of radiation had shown maximum swelling. The prepared PVA-co-poly (AMPS) hydrogels were evaluated by FT-IR, SEM, XRD, and thermal analysis (DSC and TGA). The crosslinking in components was confirmed by FT-IR, XRD, TGA and DSC analysis. The in vitro drug release was measured at wavelength of 205 nm using UV spectrophotometer. Drug release observed was higher at pH 2 than pH 7.4, due to relatively more swelling capacity at lower pH in aqueous medium. For determination of pharmacokinetic behavior, the hydrogel formulations were orally administered to rabbits. Tmax of captopril-loaded hydrogels was increased to 4 h, while Cmax was reduced to 661.853 ng/ml. The prepared polyvinyl alcohol and AMPS polymeric hydrogels may have ability to release captopril for longer duration.

polymer science