Abstract:Antiwear properties of metal and sulfur-free synergistic formulations containing quinoline derivatives (QDs)—4-N-(7-chloroquinolin-4-yl)-1-N,1-N-diethylpentane-1,4-diamine (QD-1), 4-N-(6-methoxyquinolin-8-yl)pentane-1,4-diamine (QD-2) and 1-N,1-N-diethyl-4-N-(6-methoxy quinolin-8-yl)pentane-1,4-diamine (QD-3)—with triphenyl phosphate (PE) in polyethylene glycol (PEG) at a very low concentration, 0.25% w/v of each, have been studied on a four-ball tester using ASTM D4172 and D5183 standards. Phosphorus content in the formulations was significantly reduced compared to the frequently used antiwear additive zinc dialkyldithiophosphate (ZDDP) and it was much lower than the allowed concentration suggested by various norms. The synergistic admixtures, SQD-2 and SQD-3, significantly improved the antiwear properties of base lube compared to the ZDDP/PE/QDs alone but the behavior of SQD-1 is comparable to that of ZDDP. Minimum values of mean wear scar diameter and average coefficient of friction were found to be 0.458 mm and 0.034, respectively, for SQD-3, the admixture with the maximum antiwear efficiency. However, these values were 0.538 mm and 0.083, respectively, for ZDDP, and for base oil the values were 1.185 mm and 0.126, respectively. The load-carrying capacity was found to be much higher for the synergistic formulations than for ZDDP. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) micrographs of the wear track support the tribological behavior of the above additives. The presence of nitrogen, oxygen, and phosphorus in energy-dispersive X-ray (EDX) spectra of the worn surface lubricated with SQDs indicates the adsorption of additive on the surface. The magnificent tribological behavior of SQDs may be attributed to the tribochemical film formed on the steel surface invoking phosphorus–nitrogen synergy. Quantum chemical calculations (density functional theory) for interactions of QDs with a steel surface agree well with the experimental observations.

Film Formation of Non-Phosphorus Wear Inhibitors

Antiwear Chemistry of ZDDP: Coupling Classical MD and Tight-Binding Quantum Chemical MD Methods (TB-QCMD)

Mechanical properties of tribofilms formed by metal dithiodiphosphates

Wear Mechanisms, Composition and Thickness of Antiwear Tribofilms Formed from Multi-Component Lubricants

Synergistic Effects of MoDTC and ZDTP on Frictional Behaviour of Tribofilms at the Nanometer Scale

Tribological behavior of sulfonitrided tribofilm generated from non-corrosive dimercaptobenzothiadiazole-based additives as effective boundary lubrication layer

Elucidation of the Action of Functional Groups in the Coexisting Ashless Compounds on the Tribofilm Formation and Friction Characteristic of Zinc Dialkyldithiophosphate-Formulated Lubricating Oils

Suppressed MoO3/FeMoO4 formation in molybdenum dialkyl-dithiocarbamate-derived tribofilms on nitrogen-incorporated Al-Mg-Ti-B coatings

ZDDP Tribofilm Formation and Removal

Zinc dialkyldithiophosphates adsorption and dissociation on ferrous substrates: an ab initio study

Anti-wear synergism between organomolybdenum compounds and a ZnDDP

Tribological Performance And Action Mechanism Of Cadmium Dialkyldithiophosphate

The antiwear function and mechanism cadmium dialkyldithiophosphate additive

Voltage-Assisted Tribofilm Formation of Sulfur- and Phosphorus-Free Organic Molybdenum Additive on Bearing Steel Surfaces in Industrial Base Oils

Study on Tribological Properties of Cadmium Dialkyl-Dithiophosphyl-ldithiophosphate Additive

Electrochemical Effect on Boundary Lubrication of ZDDP Additive Blended in Propylene Carbonate / Diethyl Succinate

Surface Fatigue Behavior of a WC/aC:H Thin-Film and the Tribochemical Impact of Zinc Dialkyldithiophosphate

Antiwear synergism between organomolybdenum compounds and a ZnDDP

Tribological Studies of Some Quinoline Derivatives and Their Synergistic Interaction with Phosphate Ester

The Synergistic Antiwear and Frictional Properties of Organic Molybdenum Compound with Zinc Dialkyldithiophosphate

Tribological Properties of Sulfur- and Phosphorus-Free Organic Molybdenum Compound As Additive in Oil