A novel three-dimensional network-based stearic acid/graphitized carbon foam composite as high-performance shape-stabilized phase change material for thermal energy storage

Renquan Wu,Wei Gao,Yunhong Zhou,Zhuqi Wang,Qilang Lin

DOI: https://doi.org/10.1016/j.compositesb.2021.109318

2021-11-01

Abstract:Three-dimensional porous carbon materials have received extensive attention as supports for shape-stabilized phase change materials (PCMs). In order to improve the loading capacity, thermal conductivity and encapsulation performance for PCMs, a three-dimensional graphitized carbon foam (GCF) was developed with gradient hierarchical porous surface. The GCF was successfully prepared by pyrolysis of nano-magnesium oxide/epoxy resin mixture followed by surface treatment through a carbon-thermal reaction of Fe2O3. Using the GCF prepared at 1200 °C (GCF-1200) as a support for stearic acid (SA), a novel three-dimensional network-based SA/GCF composite was achieved as shape-stabilized PCM. The results show that the GCF-1200 has a large SA loading capacity of 84.66 wt% without any liquid leakage. The prepared SA/GCF-1200 composite exhibits a good interfacial bonding between the GCF-1200 and SA without obvious phase separation in its fracture surface. The composite possesses a high compressive strength of 9.45 MPa increasing by about 3.02-fold compared with the GCF-1200, and meanwhile has a significantly improved thermal conductivity of 1.012 W/m K by 4.36 times that of pristine SA. In addition, the melting and freezing enthalpy for the composite was measured as 181.8 and 182.7 J/g, respectively, which corresponds to a thermal storage efficiency of up to 99.9%. More importantly, it presents excellent thermal reliability and chemical stability without evident changes in enthalpy after 200 thermal cycles. Therefore, the composite has a great potential for thermal energy storage applications.