Abstract:Cubic bixbyite-structured high-entropy oxides (HEOs) are regarded as potential candidates in high temperature thermal insulation field in recent years. However, their relevant properties are still needed to be explored for possible applications. In this work, twelve new high-entropy oxides (HEO1-12) of (5Re 0.2 ) 2 O 3 (Re represents five elements selected from Ce, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb) are prepared by solution combustion synthesis method combined with conventional sintering. Except HEO10 with a single monoclinic phase, other samples have a single bixbyite phase. The average grain size of bixbyite-structured samples is within 0.76 ∼ 4.96 μm. Then, the samples of HEO4, 5, 7–9 are chosen to study their mechanical and thermal properties. Their nano-modulus, nano-hardness, fracture toughness K IC , brittleness M and surface fracture energy are in the range of 152.42 ∼ 237.33 GPa, 9.22 ∼ 12.65 GPa, 1.77 ∼ 2.51 MPa·m 1/2 , 2.35 ∼ 3.09 μm −1/2 and 9.00 ∼ 22.49 J m −2 , respectively. HEO4, i.e., (Ce 0.2 Nd 0.2 Sm 0.2 Dy 0.2 Gd 0.2 ) 2 O 3 , exhibits higher K IC (1.92 MPa·m 1/2 ) and lower M (2.71 μm −1/2 ) than another reported cubic bixbyite-structured HEO of (Eu 0.2 Er 0.2 Lu 0.2 Y 0.2 Yb 0.2 ) 2 O 3 . Among the five samples, HEO4 has the lowest thermal conductivity κ (1.88 ∼ 2.55 W·m −1 ·K −1 in 25 ∼ 500 °C), which is much lower than bixbyite-structured Y 2 O 3 . In addition, HEO4 possesses a lower oxygen diffusion compared with 8YSZ in 600 ∼ 700 °C, which endows it the better oxygen barrier property. To sum up, HEO4 could be a promising candidate for high temperature thermal insulation applications due to its excellent comprehensive properties.

Effect of processing route on the crystal structure and physical properties of bixbyite high-entropy oxides

Room‐Temperature Synthesis of a Compositionally Complex Rare‐Earth Carbonate Hydroxide and its Conversion into a Bixbyite‐Type High‐Entropy Sesquioxide

Structural, mechanical and thermal properties of cubic bixbyite-structured high-entropy oxides

Thermodynamic analysis and phase characterization of high-entropy oxide Sr(Ce0.05Sn0.08Zr0.2Ti0.16Y0.3Nb0.11Al0.1)O2.9: Insights into stability, microstructure, and mechanical properties

Thermal Analysis of High Entropy Rare Earth Oxides

Preparation and Mechanical Characteristics of Multicomponent Ceramic Solid Solutions of Rare Earth Metal Oxides Synthesized by the SCS Method

Preparation and Characterization of BXFO High-Entropy Oxides

Effect of high pressure synthesis conditions on the formation of high entropy oxides

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Phase evolution and thermophysical properties of high‐entropy RE <sub>2</sub> (Y <sub>0.2</sub> Yb <sub>0.2</sub> Nb <sub>0.2</sub> Ta <sub>0.2</sub> Ce <sub>0.2</sub> ) <sub>2</sub> O <sub>7</sub> oxides

Phase evolution and thermophysical properties of high-entropy RE<sub>2</sub>(Y<sub>0.2</sub>Yb<sub>0.2</sub>Nb<sub>0.2</sub>Ta<sub>0.2 </sub>Ce<sub>0.2</sub>)<sub>2</sub>O<sub>7</sub> oxides

Preparation and High-Temperature Stability of (Zr1/5La1/5Sm1/5Dy1/5Gd1/5)O2−x High-Entropy Ceramic Materials

Phase evolution and thermophysical properties of high‐entropy RE 2 (Y 0.2 Yb 0.2 Nb 0.2 Ta 0.2 Ce 0.2 ) 2 O 7 oxides

Fluorite-structured high-entropy oxide sputtered thin films from bixbyite target

Impact of synthesis method on the structure and function of high entropy oxides

Synthesis of High Entropy Lanthanide Oxysulfides via the Thermolysis of a Molecular Precursor Cocktail

High-temperature Elemental Segregation Induced Structure Degradation in High-Entropy Fluorite Oxide

Synthesis and Thermal Decomposition of High-Entropy Layered Rare Earth Hydroxychlorides

Single-Crystalline High-Entropy Oxide Particles Synthesized via Coordination Polymerization

On the synthesis and formability of high-entropy oxides