Surface Roughening of Polystyrene and Poly(methyl methacrylate) in Ar/O2 Plasma Etching

Yuk-Hong Ting,Chi-Chun Liu,Sang-Min Park,Hongquan Jiang,Paul F. Nealey,Amy E. Wendt

DOI: https://doi.org/10.3390/polym2040649

IF: 5

2010-12-02

Polymers

Abstract:Selectively plasma-etched polystyrene-block-poly(methyl methacrylate) (PS-b-PMMA) diblock copolymer masks present a promising alternative for subsequent nanoscale patterning of underlying films. Because mask roughness can be detrimental to pattern transfer, this study examines roughness formation, with a focus on the role of cross-linking, during plasma etching of PS and PMMA. Variables include ion bombardment energy, polymer molecular weight and etch gas mixture. Roughness data support a proposed model in which surface roughness is attributed to polymer aggregation associated with cross-linking induced by energetic ion bombardment. In this model, RMS roughness peaks when cross-linking rates are comparable to chain scissioning rates, and drop to negligible levels for either very low or very high rates of cross-linking. Aggregation is minimal for very low rates of cross-linking, while very high rates produce a continuous cross-linked surface layer with low roughness. Molecular weight shows a negligible effect on roughness, while the introduction of H and F atoms suppresses roughness, apparently by terminating dangling bonds. For PS etched in Ar/O2 plasmas, roughness decreases with increasing ion energy are tentatively attributed to the formation of a continuous cross-linked layer, while roughness increases with ion energy for PMMA are attributed to increases in cross-linking from negligible to moderate levels.

polymer science