Abstract:In this work, a 0.71wt%Si+0.44wt%Al as-cast strip was produced by novel twin-roll casting. Some as-cast samples were respectively reheated and hot rolled at different temperatures in order to obtain different microstructure prior to cold rolling and annealing. The effects of the hot rolled microstructure on microstructure, texture evolution and magnetic properties were investigated in detail. A coarse deformed microstructure with λ-fiber texture was formed after hot rolling at 850–1050°C, finally leading to an inhomogeneous recrystallization microstructure with strong λ-fiber, Goss and extremely weak γ-fiber texture. By contrast, a fine transformed microstructure was formed after hot rolling at 1150–1250°C, finally leading to a fine and homogeneous recrystallization microstructure with stronger α-fiber, γ-fiber and much weaker λ-fiber texture. It should be noted that both the magnetic induction and core loss non-monotonically decreased or increased according to the hot rolling temperature. The unfavorable α-fiber and γ-fiber textures in the annealed sheets were much weaker than those of the conventional products regardless of the hot rolling temperature, thus contributing to a much higher magnetic induction. However, the average grain size in the annealed sheets was much lower than those of the conventional products regardless of the hot rolling temperature, thus leading to a higher core loss except the case of 1050°C. Hence, it is underscored that better integrated magnetic properties than those of the conventional products can be obtained by optimizing the hot rolled microstructure to produce final desirable recrystallization microstructure and texture.

Microstructural Characterization of Non-Oriented Low Silicon Steel Produced by Compact Strip Production

Microstructure, texture and magnetic properties of the semi-processed strip-cast non-oriented electrical steel

Microstructure, texture and magnetic properties of strip-cast 1.3% Si non-oriented electrical steels

Microstructure and texture evolution of thin-gauge non-oriented silicon steel with high permeability produced by twin-roll strip casting

Texture Evolution during Recrystallization and Grain Growth in Non-Oriented Electrical Steel Produced by Compact Strip Production Process

Development of thin-gauge low iron loss non-oriented silicon steel

Study on microstructure and texture of a new-type low Si high Mn non-oriented silicon steel 50W250

Characterization of microstructure, texture and magnetic properties in twin-roll casting high silicon non-oriented electrical steel

Microstructure and Texture Development in a Thin Gauge Non Oriented Electrical Steel

Microstructure and texture evolution of non-oriented electrical steel 50 W470

Development of microstructure and texture in strip casting grain oriented silicon steel

Microstructural evolution and grain refinement of a high strength low alloy steel produced by compact strip production

The Significance of Microstructure and Texture on Magnetic Properties of Non‐Oriented Silicon Steel: Strip Casting versus Conventional Process

Significant effect of as-cast microstructure on texture evolution and magnetic properties of strip cast non-oriented silicon steel

Microstructure and texture evolution of strip casting 3 wt% Si non-oriented silicon steel with columnar structure

Microstructure Characteristics and Strengthening Behavior of Cu-Bearing Non-Oriented Silicon Steel: Conventional Process versus Strip Casting

Electron Backscatter Diffraction Analysis of Low-Misorientation-Angle Boundary and High-Energy Boundary in the Hot-Rolled Plate of Grain-Orientated Silicon Steel

Effects of hot rolled microstructure after twin-roll casting on microstructure, texture and magnetic properties of low silicon non-oriented electrical steel

Microstructure and Texture Evolution of Strip-Cast and Hot-Rolled Fe-3 %si Steel Sheet

Microstructure and texture evolution of ultra-thin grain-oriented silicon steel sheet fabricated using strip casting and three-stage cold rolling method