Abstract:In this study, shot peening (SP) treatment was implemented on a duplex (austenite and ferrite) stainless steel. By using X-ray diffraction residual stress determination and line profile analysis, the residual stress (including macro- and microstress) and microstructure evolutions in the surface layer of the shot peened material were discussed. Results pointed out that the initial thermal stress state were compressive (-80 MPa) in alpha phase and tensile (90 MPa) in gamma phase owing to the different thermal expansion coefficients of the two phases. After SP, the nonreversible plastic deformation of the surface layer and the interior of bulk was the main cause of the macrostresses. SP introduced more compressive residual stress into the gamma phase, the maximum compressive stress in gamma phase was similar to 1.3 times larger than that in alpha phase (-912 vs. -717 MPa) and occurred deeper in the sample interior (similar to 75 vs. 10 mu m). The inhomogeneous partitioning of the plastic strains, which was ascribed to the difference of the relative strength and deformation mechanism between the phases, was the contributing cause of microstresses. The average microstresses in surface layer of shot peened alloy were tensile in alpha phase and compressive in gamma phase, the magnitude of which changed with depth since the phase-specific plastic deformation was also a function of depth. The quantitatively microstructural analysis indicated that more deformation was stored in the gamma phase, the microstrain and dislocation density at the surface in gamma phase were about four and 2.6 times larger than that in alpha phase (7.25 vs. 1.83 x 10(-3), 3.9 vs. 1.5 x 10(15) m(-2)), respectively. Microhardness measurements showed that SP-induced work hardening was more evident in austenite, the hardness of austenitic phase was found significantly higher than that of ferritic phase in near surface region.

Spall strength dependence on peak stress and deformation history in Lean Duplex Stainless Steel 2101

Spall Damage of A Mild Carbon Steel: Effects of Peak Stress, Strain Rate and Pulse Duration

Dependence of Spallstrength on Temperature, Grain Size and Strain Rate in Pure Ductile Metals

Deformation and Spallation of Explosive Welded Steels under Gas Gun Shock Loading

Modeling the Tensile Strain Hardening Behavior of a Metastable AISI 301LN Austenitic Stainless Steel Pre-strained in Compression

Strain Rate Dependence of Hot Tensile Behavior, Microstructure Evolution, and Fracture Mechanism of Lean Duplex Stainless Steel 2101

Surface Layer Characteristics of SAF2507 Duplex Stainless Steel Treated by Stress Shot Peening

Determination of surface mechanical property and residual stress stability for shot-peened SAF2507 duplex stainless steel by in situ X-ray diffraction stress analysis

Initiation and Propagation of Plastic Yielding in Duplex Stainless Steel

Spall Strength of 09CrNi2MoCu Steel Manufactured by Hot Rolling and Direct Laser Deposition in the Submicrosecond Loading Range

Effects of Mechanical Deformation on Dislocation Density and Phase Partitioning in 4130 Steel

Evaluation of the Residual Stress and Microstructure Character in SAF 2507 Duplex Stainless Steel after Multiple Shot Peening Process

Fracture Analysis of Ultrahigh-Strength Steel Based on Split Hopkinson Pressure Bar Test

Analysis of enhanced hydrogen embrittlement fracture for pre-strain hardening 2205 duplex stainless steel

Stress evolution in plastically deformed austenitic and ferritic steels determined using angle- and energy-dispersive diffraction

Unveiling the relationship between dislocation structure evolution and strain hardening behavior of S32654 super-austenitic stainless steel

Fatigue and tensile deformation behaviors of laser powder bed fused 304L austenitic stainless steel

Quantitative analysis of strength and plasticity of a 304 stainless steel based on the stress-strain curve

Design and Identification of High Performance Steel Alloys for Structures Subjected to Underwater Impulsive Loading

Effects of Plastic Straining on the Corrosion Resistance of TRIP-aided Lean Duplex Stainless Steels

Experimental Study on Macro- and Microstress State, Microstructural Evolution of Austenitic and Ferritic Steel Processed by Shot Peening