Quantifying the effects of grain refiners (AlTiB and Y) on microstructure and properties in W319 alloys
Xinxiu Liu,Bing Wang,Quan Li,Junsheng Wang,Chengpeng Xue,Xinghai Yang,Guangyuan Tian,Xiaoxue Chang,Xiaoguang Liu
DOI: https://doi.org/10.1016/j.mtcomm.2022.104671
IF: 3.8
2022-10-23
Materials Today Communications
Abstract:For aluminum alloys, grain refinement is the most efficient method to improve both strength and ductility. However, this rule may not apply for the recycled Al due to the large amount of intermetallics. In this paper, both secondary dendritic arm spacing (SDAS) and intermetallics have been quantified as a function of grain refinements including traditional AlTiB and most recent Y refiners. Using U-net CNN machine learning algorithm, both Fe-rich intermetallics and eutectic Si have been successfully segmented from optical and SEM/EDS images. Different from traditional refiners, (AlTiB + Y) not only strengthens the refining ability but also reduces the percentage of harmful needle-like Fe-rich intermetallics and transforms flaky Si particles into fibrous morphology. Harvested from the comprehensive grain refiners, SDAS was reduced by 38.9%, the average equivalent diameter of eutectic Si was reduced by 37.9%, and Fe-rich intermetallics content was significantly reduced. In particular, the microstructure improved by AlTiB+ 0.05Y (0.6 wt% AlTiB + 0.3 wt%Y) resulted in an increase in elongation of the refined alloy to 3.9 ± 0.4%, which is 63.3% higher compared to the base alloy, while the UTS remained at the original 260 MPa. This paper offers a promising refining technology for the recycling and casting of Al-Si alloys.
materials science, multidisciplinary