Preparation of hydroxyapatite/collagen injectable bone paste with an anti-washout property utilizing sodium alginate. Part 1: influences of excess supplementation of calcium compounds

Taira Sato,Masanori Kikuchi,Mamoru Aizawa
DOI: https://doi.org/10.1007/s10856-017-5853-3
2017-02-08
Abstract:The anti-washout property, viscosity, and cytocompatibility to an osteoblastic cell line, MG-63, of anti-washout pastes were investigated. Mixing a hydroxyapatite/collagen bone-like nanocomposite (HAp/Col), an aqueous solution of sodium alginate (Na-Alg), which is a paste hardening and lubricant agent, and supplementation of calcium carbonate or calcium citrate (Ca-Cit) as a calcium resource for the hardening reaction realized an injectable bone paste. Adding Ca-Cit at a concentration greater than eight times the Ca2+ ion concentration to Na-Alg improved the anti-washout property. Although the viscosity test indicated a gradual increase in the paste viscosity as the calcium compounds increased, pastes with excess supplementation of calcium compounds exhibited injectability through a syringe with a 1.8 mm inner diameter, realizing an injectable bone filler. Furthermore, the anti-washout pastes with Ca-Cit had almost the same cell proliferation rate as that of the HAp/Col dense body. Therefore, HAp/Col injectable anti-washout pastes composed of the HAp/Col, Na-Alg, and Ca-Cit are potential candidates for bioresorbable bone filler pastes.
What problem does this paper attempt to address?