Abstract:Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm−2) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co0.25, Ni0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm−2 at 5 mA cm−2 and a high rate retention of 69.33% at 50 mA cm−2, as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm−2. Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm−2 and a volumetric capacitance of 14.8 F cm−3 at 8 mA cm−2, as well as 1.11 F cm−2 (11.1 F cm−3) even at 50 mA cm−2. The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm−3 at the powder density of 60.1 mW cm−3. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.

Low-crystalline iron oxide hydroxide nanoparticle anode for high-performance supercapacitors

Nanostructured LiMn2O4 Composite As High-Rate Cathode for High Performance Aqueous Li-ion Hybrid Supercapacitors

A Zinc Cobalt Sulfide Nanosheet Array Derived from a 2D Bimetallic Metal-Organic Frameworks for High-Performance Supercapacitors

One-step colloid fabrication of nickel phosphides nanoplate/nickel foam hybrid electrode for high-performance asymmetric supercapacitors

Adapting a Kinetics-Enhanced Carbon Nanostructure to Li/Na Hybrid Water-in-Salt Electrolyte for High-Energy Aqueous Supercapacitors

Designing a carbon nanofiber-encapsulated iron carbide anode and nickel-cobalt sulfide-decorated carbon nanofiber cathode for high-performance supercapacitors

Oxide-doped hierarchically porous carbon for high-performance supercapacitor

High mass-loading α-Fe2O3 nanoparticles anchored on nitrogen-doped wood carbon for high-energy-density supercapacitor

Metal-like Fluorine-Doped Β-Feooh Nanorods Grown on Carbon Cloth for Scalable High-Performance Supercapacitors

N-Doped Porous Carbon-Nanofiber-Supported Fe3C/Fe2O3 Nanoparticles as Anode for High-Performance Supercapacitors

Low-crystalline mesoporous CoFe2O4/C composite with oxygen vacancies for high energy density asymmetric supercapacitors

Reduced graphite oxide wrapped ZnO-SnO 2 hollow nanospheres with as anodes for hybrid high energy density supercapacitors

Using metal–organic frameworks to create carbon-encased Ni@Ni(OH)2 for high-performance supercapacitors

Reduced graphite oxide wrapped ZnO-SnO<sub>2</sub> hollow nanospheres with as anodes for hybrid high energy density supercapacitors

High-performance aqueous asymmetric supercapacitors with a cathode of MnCo2O4 nanowires sandwiched by NiCoMnS4 nanosheets on Ni foam

Low-Cost MnO 2 Nanoflowers and La 2 O 3 Nanospheres as Efficient Electrodes for Asymmetric Supercapacitors

Nanostructured Fe 2 O 3 @C Negative Electrodes for Stable Asymmetric Supercapacitors with High-Performance

Conductive Fe@Fe2O3/FeOOH necklace-like nanowires of high electrochemical performances for a supercapacitor application

A High-Energy-Density Hybrid Supercapacitor with P-Ni(OH)2 @Co(OH)2 Core-Shell Heterostructure and Fe2 O3 Nanoneedle Arrays as Advanced Integrated Electrodes

Sodium 5-Sulfosalicylate-assisted Hydrothermal Synthesis of a Self-Supported Co3S4−Ni3S2@nickel Foam Electrode for All-Solid-state Asymmetric Supercapacitors

Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors