Abstract:We report a simple, scalable two-step method for direct-write laser fabrication of 3D, porous graphene-like carbon electrodes from polyimide films with integrated contact plugs to underlying metal layers (Au or Ni). Irradiation at high average CO2laser power (30 W) and low scan speed (∼18 mm s)-1leads to formation of 'keyhole' contact plugs through local ablation of polyimide (initial thickness 17μm) and graphitization of the plug perimeter wall. Top-surface laser-induced graphene (LIG) electrodes are then formed and connected to the plug by raster patterning at lower laser power (3.7 W) and higher scan speed (200 mm s)-1. Sheet resistance data (71 ± 15 Ω sq.)-1indicates formation of high-quality surface LIG, consistent with Raman data which yield sharp first- and second-order peaks. We have also demonstrated that high-quality LIG requires a minimum initial polyimide thickness. Capacitance data measured between surface LIG electrodes and the buried metal film indicate a polyimide layer of thickness ∼7μm remaining following laser processing. By contrast, laser graphitization of polyimide of initial thickness ∼8μm yielded devices with large sheet resistance (>1 kΩ sq.)-1. Raman data also indicated significant disorder. Plug contact resistance values were calculated from analysis of transfer line measurement data for single- and multi-plug test structures. Contacts to buried nickel layers yielded lower plug resistances (1-plug: 158 ± 7 Ω , 4-plug: 31 ± 14 Ω) compared to contacts to buried gold (1-plug: 346 ± 37 Ω , 4-plug: 52 ± 3 Ω). Further reductions are expected for multi-plug structures with increased areal density. Proof-of-concept mm-scale LIG electrochemical devices with local contact plugs yielded rapid electron transfer kinetics (rate constantk0 ∼ 0.017 cm s-1), comparable to values measured for exposed Au films (k0 ∼0.023 cm s)-1. Our results highlight the potential for integration of LIG-based sensor electrodes with semiconductor or roll-to-roll manufacturing.

Effect of laser power on the structure and specific surface area of laser-induced graphene

Effects of laser processing parameters on properties of laser-induced graphene by irradiating CO2 laser on polyimide

A Comparative Study of Laser-Induced Graphene by CO2 Infrared Laser and 355 nm Ultraviolet (UV) Laser

Investigation of micro/nano formation mechanism of porous graphene induced by CO2 laser processing on polyimide film

Laser-Induced Graphene: Synthesis Advances, Structural Tailoring, Enhanced Properties, and Sensing Applications

A review of laser-induced graphene: From experimental and theoretical fabrication processes to emerging applications

Laser induced 3D porous graphene dots: Bottom-up growth mechanism, multi-physics coupling effect and surface wettability

Influence of heat transfer at the graphene–polyimide interface on laser-induced graphene formation

The effects of low power density CO2 laser irradiation on graphene properties

Structural Modification of Single-Layer Graphene Under Laser Irradiation Featured by Micro-Raman Spectroscopy

Laser‐Induced Graphene: From Discovery to Translation

Recent Advances in Laser‐Induced Graphene: Mechanism, Fabrication, Properties, and Applications in Flexible Electronics

Insights into the surface responses of graphene oxide irradiated by an infrared femtosecond laser

Laser-Induced Graphene on Novel Crosslinked Poly(dimethylsiloxane)/Triton X-100 Composites for Improving Mechanical, Electrical and Hydrophobic Properties

Direct-write formation of integrated bottom contacts to laser-induced graphene-like carbon

Influences of CO2 Laser Modification on the Surface Morphology and Optical Absorption of Graphene Thin Films

Laser-induced graphene: preparation, functionalization and applications

Laser-induced graphene for bioelectronics and soft actuators

Laser-induced porous graphene films from commercial polymers

Probing Laser-induced Structural Transformation of Lignin into Few-layer Graphene

Controlling Thermoelectric Properties of Laser-Induced Graphene on Polyimide