Flexible, high temperature resistant and highly efficient E-heating graphene/polyimide film

Zhengwu Xu,Dewen Tang,Wenxin Shen,Rui Jiang,Mingxu Lu
DOI: https://doi.org/10.1063/5.0180858
IF: 1.697
2024-01-01
AIP Advances
Abstract:Carbon/polymer-based flexible electrothermal films, as a Joule heating material with excellent electrothermal properties, good formability, and lightweight, are a very needed material in aircraft wing de-icing systems, flexible electric heating elements, and low-voltage wearable devices. In this study, a series of flexible electrically heated films were successfully prepared using polyimide (PI) as the film-forming substrate and graphene (GE) as the conductive filler. The effects of graphene content on the morphology, microstructure, and electrothermal properties, as well as the mechanical flexibility of the electrothermal films, were systematically investigated. The results showed that the GE/PI electrothermal films not only retained the good electrical conductivity of graphene but also had the excellent mechanical properties and high heat resistance of polyimide. The electric heating film with the addition of 8 wt. % GE can quickly reach 390 °C at 24 V with uniform temperature distribution, and the mass loss at 500 °C is only 0.98 wt. %. A wide range of applications exist in fields such as flexible electric heating elements.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop a flexible, high - temperature - resistant and highly efficient electro - thermal graphene/polyimide composite film. Specifically, the research aims to prepare a composite material with excellent electro - thermal properties, mechanical flexibility and high thermal stability by adjusting the ratio of graphene (GE) to polyimide (PI). This material has broad application prospects in fields such as aircraft wing de - icing systems, flexible electric heating elements and low - voltage wearable devices. ### Main research contents: 1. **Material preparation**: Using the solution mixing method and ultrasonic - assisted technology, with polyimide as the matrix and graphene as the conductive filler, a series of composite films with different graphene contents were prepared. 2. **Performance testing**: - **Morphology and microstructure analysis**: The surface morphology and microstructure of the composite films were observed by scanning electron microscope (SEM). - **X - ray diffraction (XRD) analysis**: The crystallinity of the composite films was tested. - **Thermal stability analysis**: The mass change of the composite films at different temperatures was tested by thermogravimetric analysis (TGA). - **Infrared spectroscopy analysis (FTIR)**: The chemical structure of the composite films was detected. - **Electro - thermal performance testing**: The sheet resistance of the composite films was measured, and the temperature distribution uniformity during the heating process was observed by real - time temperature recording and infrared thermal imager. - **Mechanical performance testing**: The mechanical flexibility and heat generation uniformity of the composite films were evaluated by bending experiments. ### Research results: - **Morphology and microstructure**: As the graphene content increases, the pores in the composite films gradually disappear, and the connection between graphene sheets becomes closer, forming a good conductive network. - **XRD analysis**: The crystallinity of the composite films increases with the increase of graphene content, indicating that graphene and polyimide are well mixed. - **Thermal stability**: The mass loss of the composite film with 8 wt. % graphene content at 500 °C is only 0.98 wt. %, showing excellent high - temperature stability. - **Electro - thermal performance**: As the graphene content increases, the sheet resistance of the composite films decreases exponentially, the heating speed increases, and the steady - state temperature rises. The composite film with 8 wt. % graphene content can quickly reach 390 °C at 24 V voltage, and the temperature distribution is uniform. - **Mechanical performance**: The composite films can still maintain good electro - thermal performance in the bent state, showing excellent mechanical flexibility. ### Conclusion: By adjusting the ratio of graphene and polyimide, a flexible, high - temperature - resistant and highly efficient electro - thermal composite film was successfully prepared. This material has great application potential in fields such as multi - functional intelligent structures, flexible electric heating elements and low - voltage wearable devices.