Preparation of Mn/TiO 2 catalysts using recovered manganese from spent alkaline batteries for low-temperature NH 3 -SCR

Jenyu Jan,Chung-Liang Chang,Sue-min Chang

DOI: https://doi.org/10.1016/j.jhazmat.2024.134497

IF: 13.6

2024-05-13

Journal of Hazardous Materials

Abstract:Black mass (BM) from spent alkaline Zn-MnO 2 batteries was used for the first time as a Mn source in the preparation of Mn/TiO 2 catalysts for low-temperature NH 3 -selective catalytic reduction (SCR) of NO x . To recover Mn species and eliminate alkali and Zn species, BM powder underwent DI-water washing, followed by carbothermal reduction. The resulting slags were further dissolved in HNO 3 , loaded onto TiO 2 particles with ball milling, and then subjected to calcination. Nearly 100% of Zn species were removed from the BM via carbothermal reduction at 950 °C for 4 h with 5.0 wt% activated carbon. The resulting catalyst, derived from the treated BM, achieved similar NO x conversion (97%) as the catalyst prepared using a reagent-grade Mn chemical at 160 °C but a higher NO x -to-N 2 conversion rate at 78%. The promoted N 2 selectivity was attributed to a high Mn 4+ /Ti ratio and the presence of impurities from BM, such as Fe 3+ ions, which enhanced oxidation ability of the catalyst. Conversely, insufficient removal of Zn or carbon additives in the slags led to a decreased Mn concentration, an increased proportion of Mn 2+ /Mn 3+ species, increased surface OH groups, and reduced oxidation ability on the surface, thus reducing NO x conversion and N 2 selectivity.

environmental sciences,engineering, environmental