Abstract:This article reports the effect of pre-existing carbides prepared by different heat treatments on the nitriding behaviour during a carburizing and nitriding duplex treatment of an M50NiL steel. The goal was to achieve an improved understanding of the relationship between the pre-existing carbides and nitriding behaviour. The M50NiL steel was carburized at 950 °C, heat treated at different quenching temperatures (ranging from 1000 to 1150 °C) and tempering temperatures (ranging from 500 to 580 °C), and finally nitrided at 500 °C. The surface layers were characterized by means of X-ray diffraction (XRD), laser scanning confocal microscopy (LSCM), scanning electron microscopy (SEM), Vickers microhardness measurement and transmission electron microscopy (TEM). The results show that the formation of intergranular precipitates was greatly related to the presence of pre-existing carbides, which led to a change in the carbon content in the matrix and showed different dissolving capacities. The compound layers consisted of γ′ (Fe4N) and ε (Fe2-3N) phases as well as a minor amount of Fe3O4. The pre-existing carbides had no effect on the composition of the compound layer. For the diffusion of nitrogen, a density of pre-existing carbides that was too high or too low was unfavorable, as it greatly decreased the thickness of the nitrided layer. At the quenching temperature of 1100 °C and the tempering temperature of 540 °C, the thickest nitrided layer herein and a good hardness distribution were obtained, which was attributed to the optimum density of pre-existing carbides. This study provides information regarding how to obtain a thick nitrided layer by controlling pre-existing carbides during the duplex treatment of M50NiL steels.

Effect of pre-existing carbides prepared by different heat treatments on the nitriding behaviour during a carburizing and nitriding duplex treatment of an M50NiL steel

Effect of the carburized layer on the plasma nitriding behavior of duplex treated M50NiL steel

Nitriding behavior and mechanical properties of carburizing and nitriding duplex treated M50NiL steel

Study of M50NiL steel under carburizing and nitriding duplex treatment

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Effect of Pre-Modification by Water Jet Blasting Prior to Nitriding Vein-Like Precipitates in the Composite Diffusion Layer of M50NiL Steel

Effect of Pre-Existing VC Carbides on Nitriding and Wear Behavior of Hot-Work Die Steel

Effect of Carbon Concentration Gradient on Multi-Level Composite Microstructure and Performance of M50NiL Steel

Insights into plasma nitriding behaviour of M50NiL steel with different initial microstructures

Fabrication and mechanical properties of micro/nano-crystalline layers in M50NiL carburized steel

Optimizing the mechanical properties of M50NiL steel by plasma nitrocarburizing

Microstructure and mechanical properties of surface layer of M50NiL steel plasma nitrided

A Novel Decarburizing-Nitriding Treatment of Carburized/through-Hardened Bearing Steel towards Enhanced Nitriding Kinetics and Microstructure Refinement

Evolution of carbides on surface of carburized M50NiL bearing steel

Microstructure and mechanical properties of M50NiL steel plasma nitrocarburized with and without rare earths addition

Diffusion behavior of carbon and its hardening effect on plasma carburized M50NiL steel: Influences of treatment temperature and duration