Lawrence Berkeley National Laboratory Recent Work Title Tracking the Local Effect of Fluorine Self-Doping in Anodic TiO 2 Nanotubes Permalink
Changhai Liu,Yifan Ye,Junfa Zhu,Suidong Wang,Jinghua Guo,T. Sham
2016-01-01
Abstract:We report herein a study in which we reveal the role of F− incorporated in the very anodic TiO2 nanotubes prepared electrochemically from a Ti foil using a fluoride based electrolyte. X-ray absorption near edge structure (XANES), resonant X-ray emission spectroscopy (RXES), and X-ray photoelectron spectroscopy (XPS) have been used to examine the as-prepared and the annealed TiO2 nanotubes. It is found that the additional electron resulting from the substitution of O2− by self-doped F− in the TiO2 lattice is localized in the t2g state. Consequently, a localized Ti state can be tracked by a d−d energy loss peak with a constant energy of 1.6 eV in the RXES, in contrast to TiO2 nanostructures where this peak is hardly noticeable when F− is driven out of the lattice upon annealing. ■ INTRODUCTION As one of the solar-driven substrates for photovoltaics, TiO2 and its derivatives have been extensively developed and thoroughly investigated, to harvest their high photocatalytic efficiency, in recent decades. Various efforts have been devoted to the morphology exploration and optimization of TiO2 nanostructures associated with diverse applications. Typically, morphology engineering of TiO2 nanostructures using proper reactants via etching or doping is crucial to obtaining the equilibrium morphology with high surface stability and reactivity. Among them, F− deserves the most credit for the engineering of desired morphology for TiO2 nanostructures, particularly in the preparation of high-aspectratio TiO2 nanotubes (NTs). The use of proper fluoride electrolyte (e.g., HF, NH4F) during Ti anodization can not only form and sustain the nanotubular structure, but also optimize the NT architecture with desired geometry and alignment. The as-prepared TiO2 NTs aligned vertically on the Ti substrate provide not only the unidirectional electrical channel but also a large surface area, making this type of nanostructure a potential candidate for water-splitting, solar cell, and lithium ion battery applications, among many others. However, it appears that, in F-etched TiO2 nanostructures, a significant amount of F− ions is self-doped (trapped) into the as-prepared samples. Although these self-doped F− ions can be driven out via a heating process, they also have a desired effect on the functionality of the as-obtained TiO2 nanomaterials. As a matter of fact, TiO2 doping with fluorine has long been demonstrated both experimentally and theoretically, which results in the introduction of F 2p states and its concomitant Ti states in the band gap of TiO2, leading to the enhanced light absorption of TiO2 toward the visible and thus the increase of photoactivity. As for anodic TiO2 NTs, the amorphous form (as-grown with a large amount of F− ions) is reported to be a promising anode material for both lithium ion and sodium ion batteries, in which the self-doped F− ions and concomitant Ti species might enhance battery performances (e.g., increase charge carrier density and facilitate electron transfer). More interestingly, by applying a sealed annealing procedure, self-doped F− ions play a critical role in amorphousto-anatase phase transformation, in which amorphous TiO2 NTs will be tailored into truncated tetragonal bipyramidal Received: November 23, 2015 Revised: February 10, 2016 Published: February 16, 2016 Article