Abstract:Although the rapid development of electrical energy storage devices has slowed down environmental pollution, their large-scale application has posed huge challenges to battery-related mineral resources; thus, extending the lifespan of high-voltage lithium cobalt oxide (LCO) is of great importance. Surface oxide coating is considered as the most common low-cost modification method for addressing unstable cycling performance. However, studies have shown that the oxide layer would further react with an electrolyte, while the investigation on the corresponding component evolution is lacking. Herein, a typical example utilizing the above reaction to realize surface reconstruction is presented. Applying atomic layer deposition (ALD), originally, an ultrathin Al2O3 layer is coated on the LCO surface; however, this coating layer has undergone reconstruction after reacting with electrolyte decomposition products during the cycling. Compared with simple coating, the in situ formed Li3AlF6 layer has a tighter binding to the LCO surface while possessing good Li+ conductivity and electrochemical stability. In addition, the unique properties of the ALD technology allow us to achieve ultrathin (1 nm) and conformal coating, which is beneficial for electronic conductivity and cycling stability. Furthermore, the surface phase transition layer stripping failure mechanism has first been revealed to explain the loss of Co and O, while the reconstructed Li3AlF6 effectively suppresses the surface stripping. Thus, excellent high-voltage performance has been realized (an 89% capacity retention after 1000 cycles at 4.5 V and an 88% capacity retention after 200 cycles at 4.6 V). This work casts a new understanding on the surface reconstruction of the oxide coating layer, which is also significant for other electrode materials' modification.

Revealing the Grain-Boundary-Cracking Induced Capacity Decay of a High-Voltage LiCoO 2 at 4.6 V

Revealing the Grain-Boundary-Cracking Induced Capacity Decay of a High-Voltage LiCoO2 at 4.6 V.

Revealing the Grain-Boundary-Cracking Induced Capacity Decay of a High-Voltage LiCoO<sub>2</sub> at 4.6 V

Revealing the Accelerated Capacity Decay of a High‐Voltage LiCoO2 Upon Harsh Charging Procedure

Revealing the Accelerated Capacity Decay of a High‐Voltage LiCoO 2 upon Harsh Charging Procedure

Revealing the Accelerated Capacity Decay of a High-Voltage LiCoO<sub>2</sub> upon Harsh Charging Procedure

Realizing Superior Cycling Stability of Ni-Rich Layered Cathode by Combination of Grain Boundary Engineering and Surface Coating

Surface-interspersed nanoparticles induced cathode-electrolyte interphase enabling stable cycling of high-voltage LiCoO 2

Microscopic Investigation of Crack and Strain of LiCoO 2 Cathode Cycled under High Voltage

An in Situ Formed Surface Coating Layer Enabling LiCoO2 with Stable 4.6 V High‐Voltage Cycle Performances

Enhanced cycle stability of LiCoO2 at high voltage by mixed conductive Li7.5La3Zr1.5Co0.5O12 coating

Outside‐In Nanostructure Fabricated on LiCoO2 Surface for High‐Voltage Lithium‐Ion Batteries

Structural origin of the high-voltage instability of lithium cobalt oxide

New Insight into Bulk Structural Degradation of High-Voltage LiCoO 2 at 4.55 V

New Insight into Bulk Structural Degradation of High-Voltage LiCoO2 at 4.55 V.

Structure/Interface Coupling Effect for High‐Voltage LiCoO2 Cathodes

Preventing the Distortion of CoO6 Octahedra of LiCoO2 at High-Voltage Operation of Lithium-Ion Battery: An Organic Surface Reinforcement

Tuning Surface Chemistry to Reduce the Step-Like Degradation of LiCoO2 at 4.6 V

Ultralong Lifespan for High-Voltage LiCoO2 Enabled by In Situ Reconstruction of an Atomic Layer Deposition Coating Layer

Scalable Precise Nanofilm Coating and Gradient Al Doping Enable Stable Battery Cycling of LiCoO2 at 4.7 V

Engineering Strategies for High‐voltage LiCoO2 Based High‐energy Li‐ion Batteries