Abstract:Ultra-high nickel single-crystal cathode materials have become the most promising for lithium-ion batteries. However, the preparation of ultra-high nickel single-crystal precursors by a continuous coprecipitation method has the disadvantages of large particle size, wide distribution, poor morphology. The extent of the inhomogeneous reactions can be more severe in single-crystal cathodes with larger particle size. Herein, the coprecipitation method with a solid concentrator was adopted, and citrate sodium was used as a complexing agent to improve the physical properties of precursors and electrochemical performance of single-crystal cathode materials. By analyzing the morphology and agglomeration mechanism of the precursor nucleuses under different pH values, it was found that hexagonal nanosheets grew along the 101 direction, and the primary particles showed thicker at pH of 11.4. The hexagonal nanosheets grew along the 001 direction, and the primary particles showed finer at pH of 12.2. The morphology and particle size uniformity of the secondary particles formed by agglomeration at these two pH values showed poor. However, hexagonal nanosheets grew synergistically along the 001 and 101 directions at pH of 11.8, so the primary particles with uniform particle size gradually agglomerated, and then the secondary particles with ultra-small particle size and uniform distribution obtained. Compared to materials prepared by the traditional continuous coprecipitation method, the precursor displays a smaller particle size(D50 = 1.8 µm), higher sphericity, uniformity and denser internal structure. In order to evaluate the performance of Ni0.94Co0.04Mn0.02(OH)2 with ultra-small particle size, the sintering conditions of LiNi0.94Co0.04Mn0.02O2 need to be explored. It was found that the LiNi0.94Co0.04Mn0.02O2 cathode material prepared at 790 °C exhibited higher discharge capacity, cycle and rate performance, compared to materials prepared at 760 °C and 820 °C. We further utilized TEM, EPMA, and XPS to test the internal structure and valence state of LiNi0.94Co0.04Mn0.02O2 cathode material. The results show that the LiNi0.94Co0.04Mn0.02O2 calcined at 790 °C has a good single crystal structure. The LiNi0.94Co0.04Mn0.02O2 cathode materials inherited the structure and particle size of Ni0.94Co0.04Mn0.02(OH)2 precursors, and displayed discharge capacity of 194.7 mAh/g and capacity retention rate of 89.8 % after 100 cycles at 1 C. The microstructure and phase transition of the as-prepared cathode material are well-maintained after long-term cycling, without obvious inter-crystalline micro-crack. The results indicate that its electrochemical performance is better than that of cathode materials with precursors prepared by a continuous coprecipitation method. This work provides new insights for the preparation of small-particle-size precursor and single-crystal cathode materials.

Preparation method of high-nickel, low-cobalt and low-manganese ternary positive electrode material precursor for lithium battery

Preparation method of lithium ion battery nickel, cobalt and aluminum composite ternary cathode material

Ton-scale preparation of single-crystal Ni-rich ternary cathode materials for high-performance lithium ion batteries

Low-cost high-capacity multiple-type nickel-manganese precursor, preparation method thereof and cathode material

Ammonia-low Coprecipitation Synthesis of Lithium Layered Oxide Cathode Material for High-Performance Battery

Method for modifying lithium nickel manganese oxide positive electrode material for lithium ion battery

Surface treatment method of nickel-cobalt lithium manganate positive electrode material

Introducing an Efficient and Eco-Friendly Spray-Drying Process for the Synthesis of NCM Precursor for Lithium-ion Batteries

A Liquid and Waste-free Method for Preparing Single Crystal Positive Electrode Materials for Li-ion Batteries

Preparation method of positive electrode material for lithium-ion battery capable of improving electrochemical properties

A high performance lithium ion battery positive electrode material of a lithium iron manganese phosphate and preparation method

A highly promising high-nickel low-cobalt lithium layered oxide cathode material for high-performance lithium-ion batteries

Preparation of LiNi1/3Co1/3Mn1/3O2 cathode materials from spent Li-ion batteries

Fabrication of high electrochemical performance ternary lithium battery using LiNi0.8Co0.1Mn0.1O2 with nano-TiO2 coating

Preparation and characterization of lithium-rich ternary cathode materials using novel chelating agent and solvent

A short process and low-cost preparation of single crystal LiNi0.6Co0.2Mn0.2O2 cathode for lithium-ion batteries

A simple one-step molten salt method for synthesis of micron-sized single primary particle LiNi0.8Co0.1Mn0.1O2 cathode material for lithium-ion batteries

An Efficient Synthetic Method To Prepare High-Performance Ni-Rich Lini0.8co0.1mn0.1o2 For Lithium-Ion Batteries

Synthesis of Nickel Cobalt Manganese Ternary Transition Metal Oxide from Mixed Hydroxide Precipitate as a Precursor to NCM811

Application of precursor with ultra-small particle size and uniform particle distribution for ultra-high nickel single-crystal cathode materials by coprecipitation method

Application of Nano Al2O3 Particles As Precipitate Nucleus for Preparation of High Rate Nickel-Rich Cathode Materials