High-capacity high-Ni low-Co Li-rich layered oxides via adjusting Li 2 MnO 3 content and Li/Ni mixing defects

Zhen Wu,Kunyang Zou,Xin Dai,Yu-Han Zhang,Xudong Zhang,Hao Wang,Zhufeng Hou,Lijing Ma,Yan Liu,Yuanzhen Chen,Shengwu Guo,Yongning Liu

DOI: https://doi.org/10.1016/j.cej.2023.145986

IF: 15.1

2023-09-16

Chemical Engineering Journal

Abstract:Li-rich layered oxides (LLOs) have been considered as the promising candidate cathodes for the next high-energy Li-based batteries, but suffer from poor rate capability, lower discharge voltage, and persistent voltage fade. Appropriately increasing the Ni content in LLOs tends to improve rate capability, discharge voltage, and stability. However, the high-Ni LLOs are likely to have inferior O 2−/− redox activities, causing lower capacities, typically < 250 mAh/g. Herein, the rationally regulated Li 2 MnO 3 phase content and Li/Ni disordering defects via two-step adjustment of the Ni/Mn and Li/Mn ratios are proposed to obtain a high-capacity high-Ni low-Co LLO Li 1.167 Ni 0.222 Mn 0.537 Co 0.074 O 2 (L2-1). Compared to a typical Li 1.2 Ni 0.13 Mn 0.54 Co 0.13 O 2 (Ls), the as-prepared L2-1 cathode delivers higher reversible capacity (267.2 vs 288.2 mAh/g), higher voltage, and better rate capability. Such an improvement is demonstrated by experiments and theoretical calculations that a suitable Li 2 MnO 3 content (36.6%) and a high Li/Ni disordering (5.93%) for LLOs play a crucial role in the O 2−/− redox processes. This work contributes to the design of high-capacity high-Ni LLOs.

engineering, chemical, environmental