Low-temperature sintering and microwave dielectric properties of H3BO3-added 0.8BaSi2O5–0.2Ba3(VO4)2 composite ceramics

Ben Heng,Lifeng Ding,Dawei Wang,Chun Tong,Haikui Zhu,Lixi Wang,Yi Hou,Qitu Zhang

DOI: https://doi.org/10.1007/s10854-024-12095-5

2024-02-29

Journal of Materials Science Materials in Electronics

Abstract:In this study, 0.8BaSi 2 O 5 –0.2Ba 3 (VO 4 ) 2 composite ceramics were successfully synthesized with the addition of H 3 BO 3 ( x = 2–6 wt%) at lower temperatures using a solid-state sintering process. The phase composition and crystal structure were analyzed by X-ray diffraction, which confirmed that the addition of H 3 BO 3 did not change the phase structure of the ceramics. The composite ceramics still consisted of BaSi 2 O 5 and Ba 3 (VO 4 ) 2 . The addition of H 3 BO 3 effectively reduced the sintering temperature of the composite ceramics while maintaining the excellent microwave dielectric properties. The sintering temperature of the 0.8BaSi 2 O 5 –0.2Ba 3 (VO 4 ) 2 ceramic was reduced from 1140 to 950 °C with the addition of 3 wt% H 3 BO 3 . The 0.8BaSi 2 O 5 –0.2Ba 3 (VO 4 ) 2 –3wt%H 3 BO 3 composite ceramics, sintered at 950 °C for 4 h, exhibited the optimal microwave dielectric properties, with values of ε r = 9.23, Q×f = 33,026 GHz, and τ f = − 4.85 ppm/°C. XRD and EDS energy spectra revealed no chemical reaction between the composite ceramic and silver, highlighting its potential as a candidate for low-temperature co-fired ceramic (LTCC) applications in communications.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied