Abstract:This study presents a novel synthesis route for high-entropy alloys (HEAs) and high-entropy metallic glass (HEMG) using radio frequency (RF) magnetron sputtering and controlling the HEA phase selection according to atomic size difference (δ) and film thickness. The preparation of HEAs using sputtering requires either multitargets or the preparation of a target containing at least five distinct elements. In developing HEA-preparation techniques, the emergence of a novel sputtering target system is promising to prepare a wide range of HEAs. A new HEA-preparation technique is developed to avoid multitargets and configure the target elements with the required components in a single target system. Because of a customizable target facility, initially, a TiZrNbMoTaCr target emerged with an amorphous phase owing to a high δ value of 7.6, which was followed by a solid solution (SS) by lowering the δ value to 5 (≤6.6). Thus, this system was tested for the first time to prepare TiZrNbMoTa HEA and TiZrNbMoTa HEMG via RF magnetron sputtering. Both films were analyzed using X-ray diffraction (XRD), X-ray photoelectron spectroscopy, field emission scanning electron microscopy cross-sectional thickness, and atomic force microscopy (AFM). Furthermore, HEMG showed higher hardness 10.3 (±0.17) GPa, modulus 186 (±7) GPa, elastic deformation (0.055) and plastic deformation (0.032 GPa), smooth surface, lower corrosion current density (Icorr), and robust cell viability compared to CP-Ti and HEA. XRD analysis of the film showed SS with a body-centered cubic (BCC) structure with (110) as the preferred orientation. The valence electron concentration [VEC = 4.8 (<6.87)] also confirmed the BCC structure. Furthermore, the morphology of the thin film was analyzed through AFM, revealing a smooth surface for HEMG. Inclusively, the concept of configurational entropy (ΔSmix) is applied and the crystalline phase is achieved at room temperature, optimizing the processing by avoiding further furnace usage.

High‐Entropy Alloy Array via Liquid Metal Nanoreactor

Liquid metal for high-entropy alloy nanoparticles synthesis

Recent Progress in High‐entropy Nanocatalysts

A General Synthetic Method for High-Entropy Alloy Subnanometer Ribbons

Aerosol Synthesis of High Entropy Alloy Nanoparticles

Visualizing Formation of High Entropy Alloy Nanoparticles with Liquid Phase Transmission Electron Microscopy

Synthesis and Unique Behaviors of High-Purity HEA Nanoparticles Using Femtosecond Laser Ablation

Continuous synthesis of high-entropy alloy nanoparticles by in-flight alloying of elemental metals

Nanoprecipitate‐Strengthened High‐Entropy Alloys

Toward controllable and predictable synthesis of high-entropy alloy nanocrystals

Sparking mashups to form multifunctional alloy nanoparticles

Engineering liquid-liquid interfaces for high-entropy alloy synthesis

Hollow-Carbon Confinement Annealing: A New Synthetic Approach to Make High-Entropy Solid-Solution and Intermetallic Nanoparticles

Laser Precise Synthesis of Oxidation-Free High-Entropy Alloy Nanoparticle Libraries

Design and Development of High-Entropy Alloys with a Tailored Composition and Phase Structure Based on Thermodynamic Parameters and Film Thickness Using a Novel Combinatorial Target

Synthesis of metallic high-entropy alloy nanoparticles

Recent advances in the synthesis and fabrication methods of high-entropy alloy nanoparticles

High-Entropy Alloys – A New Era of Exploitation

A review on the rational design and fabrication of nanosized high-entropy materials

A general approach to high-entropy metallic nanowire electrocatalysts

High-entropy Alloys: an Overview on the Fundamentals, Development, and Future Perspective