Scalable Synthesis of High Entropy Alloy Nanoparticles by Microwave Heating
Haiyu Qiao,Mahmoud Tamadoni Saray,Xizheng Wang,Shaomao Xu,Gang Chen,Zhennan Huang,Chaoji Chen,Geng Zhong,Qi Dong,Min Hong,Hua Xie,Reza Shahbazian-Yassar,Liangbing Hu
DOI: https://doi.org/10.1021/acsnano.1c05113
IF: 17.1
2021-08-23
ACS Nano
Abstract:High entropy alloy nanoparticles (HEA-NPs) are reported to have superior performance in catalysis, energy storage, and conversion due to the broad range of elements that can be incorporated in these materials, enabling tunable activity, excellent thermal and chemical stability, and a synergistic catalytic effect. However, scaling the manufacturing of HEA-NPs with uniform particle size and homogeneous elemental distribution efficiently is still a challenge due to the required critical synthetic conditions where high temperature is typically involved. In this work, we demonstrate an efficient and scalable microwave heating method using carbon-based materials as substrates to fabricate HEA-NPs with uniform particle size. Due to the abundant functional group defects that can absorb microwave efficiently, reduced graphene oxide is employed as a model substrate to produce an average temperature reaching as high as ∼1850 K within seconds. As a proof-of-concept, we utilize this rapid, high-temperature heating process to synthesize PtPdFeCoNi HEA-NPs, which exhibit an average particle size of ∼12 nm and uniform elemental mixing resulting from decomposition nearly at the same time and liquid metal solidification without diffusion. Various carbon-based materials can also be employed as substrates, including one-dimensional carbon nanofibers and three-dimensional carbonized wood, which can achieve temperatures of >1400 K. This facile and efficient microwave heating method is also compatible with the roll-to-roll process, providing a feasible route for scalable HEA-NPs manufacturing.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsnano.1c05113.Digital images of the microwave process and the demonstration of plasma, SEM images of precursor/rGO-570 film, CNFs, and c-wood, particle size distribution of precursor particles and HEA-NPs, XRD spectra of the precursor/rGO-570 film and PtPdFeCoNi HEA-NPs/CNFs, Raman spectra of rGO with different degrees of defects, CNFs, and c-wood, FFT image calculated from HRTEM of PtPdFeCoNi HEA-NPs/rGO and PtPdFeCoNi HEA-NPs/c-wood, high-speed video image and light intensity of CNFs and c-wood during microwave heating, FR-IR spectra of CNFs and c-wood, TEM images of PtPdFeCoNi HEA-NPs/CNFs and HEA-NPs/c-wood, HAADF-STEM image and STEM-EDS elemental mapping of PtPdFeCoNi HEA-NPs/CNFs and HEA-NPs/c-wood, TGA analysis of PtPdFeCoNi HEA-NPs/c-wood; table summarizing the physicochemical properties of elemental precursor salts and corresponding metals, table of details and results of control experiments of rGO with different size and different degree of defects, table of reported lattice constant and d-spacings of pure metal and HEA-NPs/rGO, and table summarizing reported synthesized HEA-NPs composition, method, and crystal structure (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology