Abstract:A mild route has been developed to partially oxidize Ti3C2Tx by introducing O2 molecules during refluxing Ti3C2Tx suspension. The subsequent etching away of TiO2 nanoparticles leaves behind abundant in‐plane nanopores which not only increase electroactive sites but also significantly improve ion kinetics. Thus, the holey Ti3C2Tx film exhibits less‐dependence capacitive performance even with film thickness up to 84 μm. The Ti3C2Tx film with metallic conductivity and high pseudo‐capacitance holds profound promise in flexible high‐rate supercapacitors. However, the restacking of Ti3C2Tx sheets hinders ion access to thick film electrodes. Herein, a mild yet green route has been developed to partially oxidize Ti3C2Tx to TiO2/Ti3C2Tx by introducing O2 molecules during refluxing the Ti3C2Tx suspension. The subsequent etching away of these TiO2 nanoparticles by HF leaves behind numerous in‐plane nanopores on the Ti3C2Tx sheets. Electrochemical impedance spectroscopy shows that longer oxidation time of 40 min yields holey Ti3C2Tx (H‐Ti3C2Tx) with a much shorter relax time constant of 0.85 s at electrode thickness of 25 μm, which is 89 times smaller than that of the pristineTi3C2Tx film (75.58 s). Meanwhile, H‐Ti3C2Tx film with 25 min oxidation exhibits less‐dependent capacitive performance in film thickness range of 10–84 μm (1.63–6.41 mg cm−2) and maintains around 60% capacitance as the current density increases from 1 to 50 A g−1. The findings clearly demonstrate that in‐plane nanopores not only provide more electrochemically active sites, but also offer numerous pathways for rapid ion impregnation across the thick Ti3C2Tx film. The method reported herein would pave way for fabricating porous MXene materials toward high‐rate flexible supercapacitor applications.

Optimizing Ion Pathway in Titanium Carbide MXene for Practical High‐Rate Supercapacitor

Achieving Quick Charge/discharge Rate of 3.0 V S−1 by 2D Titanium Carbide (mxene) Via N-doped Carbon Intercalation

Tuning the Pore Size Distribution of Ti3C2Tx Porous Film for High Capacity Supercapacitor Electrode

Laser writing of the restacked titanium carbide MXene for high performance supercapacitors

Tuning the pore size distribution of Ti3C2T porous film for high capacity supercapacitor electrode

Thickness‐Independent Capacitive Performance of Holey Ti3C2Tx Film Prepared through a Mild Oxidation Strategy

Enhanced Rate Capability of Ion‐Accessible Ti3C2Tx‐NbN Hybrid Electrodes

High-Mass-Loading Porous Ti3C2Tx Films for Ultrahigh-Rate Pseudocapacitors

Vertically pillared V2CT /Ti3C2T flexible films for high-performance supercapacitors

Porosity-adjustable MXene film with transverse and longitudinal ion channels for flexible supercapacitors

Hierarchical porous MXene film with diffusion path optimization for supercapacitor

In situ Modified Mesoporous MXene Film with Excellent Oxidation Resistance for High-Performance Supercapacitor

Aggregation‐Resistant 3D Ti 3 C 2 T x MXene with Enhanced Kinetics for Potassium Ion Hybrid Capacitors

Enhanced supercapacitive performance of manganese oxides doped two-dimensional titanium carbide nanocomposite in alkaline electrolyte

Enhancing Capacitance Performance of Ti3C2Tx MXene as Electrode Materials of Supercapacitor: From Controlled Preparation to Composite Structure Construction

MXene nanomesh for high-performance supercapacitor

A Novel Sandwiched Porous MXene/Polyaniline Nanofibers Composite Film for High Capacitance Supercapacitor Electrode

Achieving High Pseudocapacitance of 2D Titanium Carbide (mxene) by Cation Intercalation and Surface Modification

New Ti3-yNbyC2Tx MXenes As High-Rate and Ultra-Stable Electrode Materials for Supercapacitors

Recycling Ti3C2Tx Oxide Nanosheets Through Channel Engineering: Implications for High-Capacity Supercapacitors

Ti3−yNbyC2T MXenes as high-rate and ultra-stable electrode materials for supercapacitors