Porosity-adjustable MXene film with transverse and longitudinal ion channels for flexible supercapacitors

Daotong Zhang,Min Luo,Kai Yang,Pei Yang,Chaozheng Liu,Weimin Chen,Xiaoyan Zhou

DOI: https://doi.org/10.1016/j.micromeso.2021.111389

IF: 5.876

2021-10-01

Microporous and Mesoporous Materials

Abstract:Ti3C2T x (a typical MXene) films can be used as free-standing electrodes due to their ultrahigh electrical conductivity, well flexibility and high electrochemical activity. However, inevitable self-restacking issue of Ti3C2T x nanosheets largely decreases exposed area and impedes the ion transport in Ti3C2T x film. Herein, hierarchically porous carbon (HPC) introduced into Ti3C2T x film can not only act as the pillar for adjacent Ti3C2T x nanosheets to prevent their typical self-restacking and further accelerate rapid ion transport in the transverse direction, but also ensure rapid ion transport in the longitudinal direction by introducing abundant macro/mesopores. By easily changing the amount of HPC (0–60%), the porosity of the film is well controlled, with adjustable specific surface area (SSA) from 8 m2 g−1 to 755 m2 g−1. The prepared quasi-solid-state supercapacitor fabricated by 60% HPC shows a good stability after different bending angles, high capacitance of 211 mF cm−2, energy density of 4.68 μW h cm−2 at 19.91 μW cm−2, and high capacitance retention of 86% after 10,000 charging-discharging cycles. This work will pave a facile route to alleviate the self-restacking phenomenon of Ti3C2T x film by constructing transverse and longitudinal channels for rapid ion transport.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied