Effect of cellulose nanocrystals on the mechanical and free vibration behavior of hybrid glass/kenaf fiber reinforced polyurethane core-based sandwich structures

Eashwar Raaj K,Jesuarockiam Naveen,N. Karthikeyan,Tabrej Khan,Tamer A. Sebaey

DOI: https://doi.org/10.1080/15440478.2024.2361311

2024-06-06

Journal of Natural Fibers

Abstract:Engineering applications widely use foam-core-based sandwich structures. The study incorporated cellulose nanocrystals (CNC) into a hybrid glass/kenaf fiber-based polymeric sandwich structure with a 65 kg/m3 polyurethane foam core. Four unique face sheets (S1, S2, S3, and S4) were made using glass, kenaf, and CNC. Three-point bending, Charpy impact testing, and free vibration testing were used to characterize sandwich structures. The inclusion of CNC in the matrix of face sheets improved the hybrid composite's bending strength and impact resistance. One layer of Kenaf fabric and two layers of glass make up the hybrid composite, which is stronger in both flexural strength and impact resistance, with 14.56 MPa and 8.1 J, respectively. These improvements are 44.84% and 57.49% compared to the pure glass/epoxy composite face plate. Nevertheless, the incorporation of Computer Numerical Control (CNC) failed to result in a substantial enhancement in vibration characteristics. Both matrix modification and natural fiber (kenaf) can effectively substitute glass fabric in sandwich structures. 工程应用广泛使用基于泡沫芯的夹层结构。该研究将纤维素纳米晶体(CNC)掺入具有65 kg/m3聚氨酯泡沫芯的混合玻璃/红麻纤维基聚合物夹层结构中. 四个独特的面板(S1、S2、S3和S4)使用玻璃、红麻和CNC制成. 采用三点弯曲、夏比冲击试验和自由振动试验对夹层结构进行了表征. 在面板基体中加入CNC提高了混合复合材料的抗弯强度和抗冲击性. 一层红麻织物和两层玻璃构成了混合复合材料,其弯曲强度和抗冲击性都更强,分别为14.56MPa和8.1J. 与纯玻璃/环氧树脂复合面板相比,这些改进分别为44.84%和57.49%. 然而,计算机数字控制(CNC)的结合未能显著提高振动特性. 基质改性和天然纤维(红麻)都能有效地替代夹层结构中的玻璃纤维.

materials science, textiles

What problem does this paper attempt to address?

The paper primarily explores the effects of Cellulose Nanocrystals (CNC) on the mechanical properties and free vibration behavior of hybrid glass/kenaf fiber-reinforced polyurethane foam core sandwich structures.

Specifically, the researchers aimed to improve the flexural strength and impact resistance of the sandwich structures by adding cellulose nanocrystals to the face layers. They prepared four different face layers (S1, S2, S3, and S4), which included varying proportions of glass fiber, kenaf fiber, and cellulose nanocrystals. The experimental results showed:

1. **Flexural Strength**: The hybrid composites containing cellulose nanocrystals (e.g., S2 and S3 samples) exhibited an increase in flexural strength by 44.84% and 37.11%, respectively, compared to the pure glass/epoxy composite (S1 sample).

2. **Impact Resistance**: Similarly, in terms of impact resistance, the S2 and S3 samples showed improvements of 57.79% and 44.81%, respectively, compared to the S1 sample.

3. **Free Vibration Characteristics**: However, the addition of cellulose nanocrystals did not significantly improve the vibration characteristics.

4. **Optimal Configuration**: The hybrid composite consisting of one layer of kenaf fabric and two layers of glass exhibited the best performance, with a flexural strength of 14.56 MPa and an impact resistance of 8.1 J, which are improvements of 44.84% and 57.49%, respectively, over the pure glass/epoxy composite panel.

In summary, the study aims to enhance the mechanical properties of foam core-based sandwich structures by introducing cellulose nanocrystals and finds that this enhancement is very effective in improving flexural strength and impact resistance, but not as effective in improving vibration characteristics. Additionally, the research highlights the potential of matrix modification and the use of natural fibers (such as kenaf) as alternative materials in sandwich structures.