Abstract:This study presents a nitrogen-doped microporous carbon nanospheres (N@MCNs) prepared by a facile polymerization–carbonization process using low-cost styrene. The N element in situ introduces polystyrene (PS) nanospheres via emulsion polymerization of styrene with cyanuric chloride as crosslinking agent, and then carbonization obtains N@MCNs. The as-prepared carbon nanospheres possess the complete spherical structure and adjustable nitrogen amount by controlling the relative proportion of tetrachloromethane and cyanuric chloride. The friction performance of N@MCNs as lubricating oil additives was surveyed utilizing the friction experiment of ball-disc structure. The results showed that N@MCNs exhibit superb reduction performance of friction and wear. When the addition of N@MCNs was 0.06 wt%, the friction coefficient of PAO-10 decreased from 0.188 to 0.105, and the wear volume reduced by 94.4%. The width and depth of wear marks of N@MCNs decreased by 49.2% and 94.5%, respectively. The carrying capacity of load was rocketed from 100 to 400 N concurrently. Through the analysis of the lubrication mechanism, the result manifested that the prepared N@MCNs enter clearance of the friction pair, transform the sliding friction into the mixed friction of sliding and rolling, and repair the contact surface through the repair effect. Furthermore, the tribochemical reaction between nanoparticles and friction pairs forms a protective film containing nitride and metal oxides, which can avert direct contact with the matrix and improve the tribological properties. This experiment showed that nitrogen-doped polystyrene-based carbon nanospheres prepared by in-situ doping are the promising materials for wear resistance and reducing friction. This preparing method can be ulteriorly expanded to multi-element co-permeable materials. Nitrogen and boron co-doped carbon nanospheres (B,N@MCNs) were prepared by mixed carbonization of N-enriched PS and boric acid, and exhibited high load carrying capacity and good tribological properties.

Nitrogen-doped porous carbon nanospheres derived from hyper-crosslinked polystyrene as lubricant additives for friction and wear reduction

In-situ formation of nitrogen doped microporous carbon nanospheres derived from polystyrene as lubricant additives for anti-wear and friction reduction

Silica-Coated N-Doped Porous Carbon Nanospheres as Antiwear and Friction-Reduction Lubricant Additives

Polystyrene-derived porous graphite carbon nanospheres with corrosion resistance as a lubricant additive for efficient friction and wear reduction

Sulfur-Containing Carbon Nanospheres as Lubricant Additives for Antiwear and Friction Reduction

Nitrogen-Doped Carbon Dot as a Lubricant Additive in Polar and Non-polar Oils for Superior Tribological Properties via Condensation Reaction

Enhanced lubricity and anti-wear performance of zwitterionic polymer-modified N-enriched porous carbon nanosheets as water-based lubricant additive

Zwitterionic polymer-functionalized nitrogen-doped MXene nanosheets as aqueous lubricant additive

Tribological Performance of Nanocomposite Carbon Lubricant Additive

Tribological performance and lubrication mechanism of carbon nitride nanosheets as novel and high-efficiency additives for water lubrication

Ionic Nitrogen-Doped Carbon Dots as Nonpolar Lubricant Additives at Low Effective Addition

Anti-wear and Friction Reducing Mechanisms of Carbon Nano-onions as Lubricant Additives

Synergistic friction-reduction and wear-resistance mechanism of 3D graphene and SiO2 nanoblend at harsh friction interface

Effect of g-C3N4 morphology on its performance as lubricating additive for grease

Structural, Mechanical and Tribological Properties of Mo–S–N Solid Lubricant Films

Synergistic Effects of Carbon Nanotube/Nano-MoS2 Hybrid on Tribological Performance of Polyimide Nanocomposite Films

Tribological Properties of CNT microspheres as a Lubricant Additive

Fabrication of DDP-functionalized carbon nitride nanosheets via thiol-ene "click" reaction as lubricant additives

Synthetic Kilogram Carbon Dots for Superior Friction Reduction and Antiwear Additives

Rich activated edges of hexagonal boron nitride flakes in-situ triggered by nickel nanoparticles to achieve efficient reduction of friction and wear

Tribological Property of Biocarbon-Based Magnesium Silicate Hydroxide Nanocomposite as Lubricant Additive at Different Concentrations of Additive and Dispersant